Abstract:In recent years, weight reduction of automobile bodies has been effective in reducing carbon dioxide emissions. For this reason, the replacement of steel, which has a large specific gravity, with aluminum alloys and carbon fiber reinforced plastics is being promoted for the right materials in the right places. In this case, an appropriate dissimilar material joining method is needed in terms of ease of assembly, joining performance, and cost. Friction stir welding (FSW) has emerged as a promising joining method for a variety of engineering applications. FSW is a solid-phase joining technique that has been shown to have significant advantages over conventional welding in terms of the strength and quality of the joints produced. However, during joining of metallic materials by FSW, microstructural changes may occur that affect their corrosion degradation. In this study, the corrosion behavior of A6061 jointed with high-strength steel (SPCC980) by FSW in aqueous NaCl solution and the effect of Al alloy microstructural changes on it were investigated. In this study, FSW was performed on A6061 and SPCC980 steel plates, and galvanic corrosion behavior was investigated by immersion tests and surface observations, as well as electrochemical measurements of Al alloys. Immersion tests were performed in 1 M NaCl solution. Micro electrochemical polarization tests of A6061 were also performed to investigate the corrosion behavior. In the immersion test of the galvanic couple of A6061 and SPCC980 steel plates in NaCl solution, galvanic corrosion occurred with the Al alloy as the anode and the steel plate as the cathode, and hydrogen evolution was observed mainly from the BM site on A6061 in the initial stage of immersion. This is due to the hydrogen evolution reaction occurring inside the pitting corrosion of the A6061. The pits was formed near Fe-rich inclusions in the BM site. In the HAZ site, corrosion propagated from Fe-rich inclusions along grain boundaries, but no pitting corrosion was formed. In the NZ site, minor localized corrosion was developed. These results indicate that the susceptibility to localized corrosion and its morphology differ in each site on the A6061. The difference in localized corrosion susceptibility on the A6061 was considered to be caused by the difference in the distribution of Fe-rich inclusions. However, the fact that the size and number of Fe-rich inclusions in each site did not differ suggests that the difference in anodic dissolution activity near Fe-rich inclusions affects pitting corrosion susceptibility in each site. A6061 alloy is a precipitation-strengthened Al alloy reinforced by β'' phase, which is a metastable phase of Mg 2 Si, and dense precipitation of β'' phase was observed in the BM site. Therefore, the reason for the higher localized corrosion susceptibility of BM is related to the precipitation of the β'' phase. This paper is based on results obtained from a project, JPNP14014, commissioned by the New Energy and Industrial Technology Development Organization (NEDO).

Correlating corrosion modes with the microstructure of the 2XXX series alloys: A comparative approach

Microstructural, Electrochemical and Localized Corrosion Characterization of the AA2198-T851 Alloy

Corrosion Behavior of Aluminum Alloys in Different Alkaline Environments: Effect of Alloying Elements and Anodization Treatments

Multi-scale study on the electrochemical behavior and corrosion mechanism of 5083 aluminum alloy with different microstructures in a NaCl environment

Understanding the Effect of Corrosion Resistance in Welded AA2198‐T8 Alloy: Microstructural‐Electrochemical Insights

Correlation of microstructure with corrosion performance in high zinc 7068 aluminum alloy aged using different T6 conditions

Study on the Correlation between the Microstructure Characteristics and Corrosion Behaviors of 2A12-T4 Aluminum Alloy under Thermal Strain

Influence of β-Mg 17 Al 12 and Al-Mn intermetallic compounds on the corrosion behaviour of cast and solution treated Mg-Al-Zn-Mn alloys

Investigation of Long-term Corrosion of AA2024 and AA5119 Aluminum Alloys under chromate coating in Marine Atmosphere by Electrochemical Impedance Technology

Corrosion Susceptibility of Passive Films on 1060, 2024, and 5083 Aluminum Alloys: Experimental Study and First-Principles Calculations

Grain-interior corrosion and tensile performance degradation of 2XXX Al–Li alloy in an actual marine environment

Assessment of the Corrosion Behavior of Friction-Stir-Welded Dissimilar Aluminum Alloys

A novel technique to examine the corrosion resistance of FSW dissimilar aluminium alloys under three different corrosion solutions

A mechanistic study on localized corrosion of sandwich multi-layered aluminium sheet in 3.5 wt.% NaCl solution

Microstructure Evolution and the Resulted Influence on Localized Corrosion in Al-Zn-Mg-Cu Alloy during Non-Isothermal Ageing

Comparative study of corrosion susceptibility and microstructural effects on AA7075-T6 aluminum alloys under different heat treatments

Corrosion Behavior of Al Alloy A6061 Jointed with High-Tensile Strength Steel By Friction Stir Welding in NaCl Solution

Quantitative study of the corrosion evolution and stress corrosion cracking of high strength aluminum alloys in solution and thin electrolyte layer containing Cl-

Corrosion of Aluminum Alloy Metal Matrix Composites in Neutral Chloride Solutions

Corrosion property of Al alloys subjected to surface severe plastic deformation: a review

Corrosion evaluation of Al-Cu-Mn-Zr cast alloys in 3.5% NaCl solution