Abstract:To explore the effect of nano-attapulgite clay (NAC) on the durability of concrete, two kinds of NAC (calcined raw ore and calcined high viscosity ore: calcination at 650 °C for 2 h) were used to study their effects on the durability of concrete, mainly discussing the changes of chloride ion permeability and the resistivity of concrete with NAC. The effect of NAC on the strength of concrete was analyzed by testing the compressive strength of concrete. The two-electrode method, four-electrode method, and concrete resistivity tester were used to analyze the relationship between the testing method and concrete resistivity, and the effect of NAC on concrete resistivity was analyzed. The influence of NAC on the chloride corrosion resistance of concrete was analyzed by measuring the chloride diffusion coefficient, and the relationship between the chloride diffusion coefficient and resistivity was established. The diffusion process of chloride ions in concrete was analyzed by theoretical derivation and numerical simulation. The results show that: calcining raw ore NAC can improve the compressive strength of concrete, while calcining high-viscosity ore reduces the compressive strength of concrete. At the age of 28 days, the strength of concrete mixed with calcined raw ore is about 7.10% higher than that of ordinary concrete, while the compressive strength of concrete mixed with calcined high-viscosity ore is about 4.32% lower than that of common concrete. The resistivity of concrete mixed with calcined raw ore increases the fastest, and the 56 days age is about 15.8% and 29.6% higher than that of ordinary concrete and calcined high-viscosity ore. There is a good negative correlation between concrete resistivity and chloride diffusion coefficient. At 28 days, the incorporation of calcined raw ore concrete decreased by about 19.9% and 49.4% compared with ordinary concrete and calcined high-viscosity ore, respectively. After 10 years of decline, the chloride ion content is 11.1% and 23.2% lower than that of ordinary concrete and concrete mixed with calcined high viscosity ore.

Cl- attack resistance of marine concrete with nano-particles under the combined action of flexural fatigue load and freeze-thaw cycles

Study on the durability of marine concrete with nanoparticles under the coupling action of bending fatigue load, dry-wet cycles and Cl − corrosion

Interaction Effect of Chloride Attack and Carbonization in Concrete

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Long term effect of corrosion inhibitor and associated cation type of chloride ions on chloride profile of concrete exposed to composite chloride-sulfate environment

Optimal Design and Performance of Concrete with Function Component in Marine Environment

Influence of the Coupling Action of Flexural Load and Freezing–Thawing on the Chloride Diffusion of Marine High-Performance Concrete

The Resistance of Novel Concrete Prepared by Gap-Graded Blended Cement under Chloride-Sulfate Attack

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Chloride ion penetration resistance of concrete containing fly ash and silica fume against combined freezing-thawing and chloride attack

Effect of nano-silica as cementitious materials-reducing admixtures on the workability, mechanical properties and durability of concrete

Study on Concrete Deterioration and Chloride Ion Diffusion Mechanism by Different Aqueous NaCl-MgSO4 Concentrations

Study on the Relationship between Chloride Ion Penetration and Resistivity of NAC-Cement Concrete

Research progress in mechanisms and properties of nano-modified interface transition zone of Marine concrete

Study on the Frost Resistance of Composite Limestone Powder Concrete against Coupling Effects of Sulfate Freeze–Thaw

Study on Concrete Deterioration in Different NaCl-Na2SO4 Solutions and the Mechanism of Cl- Diffusion

Improved mechanical response of Nano-SiO2 powder cemented soil under the coupling effect of dry and wet cycles and seawater corrosion