Long term effect of corrosion inhibitor and associated cation type of chloride ions on chloride profile of concrete exposed to composite chloride-sulfate environment

Jyotish Kumar Das,Bulu Pradhan
DOI: https://doi.org/10.1016/j.matpr.2020.04.014
2020-01-01
Materials Today: Proceedings
Abstract:This paper experimentally investigated the effect of nitrite-based corrosion inhibitor and cation type namely Na+, Mg2+ and Ca2+ associated with chloride ions on free chloride (CF) and total chloride (CT) ion concentrations of concrete exposed to composite chloride-sulfate ( C l - + S O 4 2 - ) environment. Concrete cubes were prepared using Portland pozzolana cement and w/c ratio of 0.55. Sodium nitrite (NaNO2) was used as a corrosion inhibitor at an admixed dosage of 3% by weight of cement. After curing, the cubes were subjected to composite C l - + S O 4 2 - solutions such as NaCl + MgSO4, MgCl2 + MgSO4, and CaCl2 + MgSO4. Powder samples were collected at different depth intervals from the cubes to determine the CF and CT concentrations. Fourier transform infrared (FTIR) spectroscopy and Field emission scanning electron microscope (FESEM) analyses were carried to examine the microstructure of concrete. The experimental results indicated that addition of NaNO2 in concrete reduced the penetration of chloride ions. Concrete exposed to CaCl2 + MgSO4 solution mostly showed higher CF and CT concentrations than NaCl + MgSO4 solution followed by MgCl2 + MgSO4 solution. Results of microstructure study indicated the formation of different compounds in concrete exposed to composite C l - + S O 4 2 - solutions.
What problem does this paper attempt to address?