Abstract:Plastic deformation of low/high density polyethylene (LDPE/HDPE) was analyzed in this work using positron annihilation lifetime spectroscopy (PALS). It was shown that in undeformed LDPE, both the mean ortho-positronium lifetime (τ3) and its dispersion (σ3), corresponding to the average size and size distribution of the free-volume pores of the amorphous component, respectively, were clearly higher than in HDPE. This effect was induced by a lower and less uniform molecular packing of the amorphous regions in LDPE. During the deformation of LDPE, an increase in the τ3 value was observed within the local strains of 0–0.25. This effect was mainly stimulated by a positive relative increase in interlamellar distances due to the deformation of lamellar crystals oriented perpendicular (increased by 31.8%) and parallel (decreased by 10.1%) to the deformation directions. At the same time, the dimension of free-volume pores became more uniform, which was manifested by a decrease in the σ3 value. No significant effect of temperature or strain rate on the τ3 and σ3 values was observed during LDPE deformation. In turn, in the case of HDPE, with an increase in the strain rate/or a decrease in temperature, an intensification of the cavitation phenomenon could be observed with a simultaneous decrease in the τ3 value. This effect was caused by the lack of annihilation of ortho-positonium (o-Ps) along the longer axis of the highly anisotropic/ellipsoidal cavities. Therefore, this dimension was not detectable by the PALS technique. At the same time, the increase in the dimension of the shorter axis of the cavities was effectively limited by the thickness of amorphous layers. As the strain rate increased or the temperature decreased, the σ3 value during HDPE deformation increased. This change was correlated with the initiation and intensification of the cavitation phenomenon. Based on the mechanical response of samples with a similar yield stress, it was also proven that the susceptibility of the amorphous regions of LDPE to the formation of cavities is lower than in the case of amorphous component of HDPE.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the changes in the microscopic mechanisms of polyethylene (including low - density polyethylene LDPE and high - density polyethylene HDPE) during uniaxial tensile deformation under different strain rates and temperature conditions, especially the changes in the size and distribution of free - volume pores in the amorphous region. The research uses positron annihilation lifetime spectroscopy (PALS) technology to analyze these changes, aiming to fill the knowledge gap regarding the microstructural changes in the initial deformation stage of semi - crystalline polymers. Specifically, the paper focuses on the following aspects: 1. **The influence of strain rate and temperature on the microscopic deformation mechanisms of LDPE and HDPE plastics**: The research explores the differences in the microscopic behaviors of LDPE and HDPE during plastic deformation under different strain rates and temperature conditions, especially the changes in the size and distribution of free - volume pores in the amorphous region. 2. **The application of PALS technology**: By using PALS technology, researchers can measure and analyze the size and distribution of free - volume pores in materials, which is one of the key parameters for understanding the changes in the microstructure of materials. 3. **The comparison between LDPE and HDPE**: By comparing the performance of two polyethylene materials with different densities under the same conditions, the research reveals how the microstructure of materials (such as crystallinity, crystal thickness, and amorphous layer thickness) affects their macroscopic mechanical properties, especially the occurrence of plastic deformation and cavitation phenomena. 4. **The mechanism of the cavitation phenomenon**: The research also delves into the mechanism of the cavitation phenomenon, especially the influence of the occurrence and development of cavitation on the mechanical properties of materials under different strain rates and temperature conditions. In summary, through detailed experimental design and data analysis, this paper aims to deepen the understanding of the microscopic behaviors of polyethylene materials under different deformation conditions, providing theoretical support and technical guidance for materials science and engineering applications.

Strain Rate and Temperature Influence on Micromechanisms of Plastic Deformation of Polyethylenes Investigated by Positron Annihilation Lifetime Spectroscopy

A Constitutive Model for Strain Hardening Behavior of Predeformed Amorphous Polymers: Incorporating Dissipative Dynamics of Molecular Orientation

Aging-dependent Strain Localization in Amorphous Glassy Polymers: from Necking to Shear Banding

Deformation Mechanisms of Polymer Thin Films by Simultaneous Kinetic Measurement of Microscopic Infrared Dichroism and Macroscopic Stress. Part Iii: Influence of Morphology on Molecular Orientation of Isotactic Polypropylene Films Subjected to Uniaxial Stretching

Deformation Mechanisms of Polymer Thin Films by Simultaneous Kinetic Measurement of Microscopic Infrared Dichroism and Macroscopic Stress. 2. Molecular Orientation During Necking Process of Isotactic Polypropylene

Morphology and Plastic Yielding of Ultrahigh Molecular Weight Polyethylene

Deformation and Molecular Orientation in Films of Metallocene Polypropylene, Ethylene-Butylene Rubber, and Their 80/20 (W/W) Blend Revealed by the Simultaneous Kinetic Measurement of Microscopic Infrared Dichroism, Macroscopic Stress, and Mesoscale Strain

The effect of strain rate on the viscoplastic behavior of isotactic polypropylene at finite strains

Segmental Orientations and Deformation Mechanism of Poly(Ether-Block-Amide) Films

Strain effects on thermal transitions and mechanical properties of thermoplastic polyurethane elastomers

Effects of Spinodal Decomposition on Mechanical Properties of A Polyolefin Blend from High to Low Strain Rates

Critical Strains for Lamellae Deformation and Cavitation During Uniaxial Stretching of Annealed Isotactic Polypropylene

Polypropylene/polyamide 6/polyethylene–octene Elastomer Blends. Part 2: Volume Dilatation During Plastic Deformation under Uniaxial Tension

Molecular dynamics simulation of plastic deformation in polyethylene under uniaxial and biaxial tension

Effect of Plasticization/Annealing on Thermal, Dynamic Mechanical, and Rheological Properties of Poly(Lactic Acid)

Polypropylene/Polyamide 6/Polyethylene-Octene Elastomer Blends. Part 3. Mechanisms of Volume Dilatation During Plastic Deformation under Uniaxial Tension

Unraveling the Effect of Strain Rate and Temperature on the Heterogeneous Mechanical Behavior of Polymer Nanocomposites via Atomistic Simulations and Continuum Models

Thermomechanical coupling during large strain deformation of polycarbonate: Experimental study

Tensile Behavior of High-Density Polyethylene Including the Effects of Processing Technique, Thickness, Temperature, and Strain Rate

Rate-dependent Constitutive Model of Poly(ethylene Terephthalate) for Dynamic Analysis

Plastic damage mechanisms of polypropylene/polyamide 6/polyethelene-octene elastomer blends under cyclic tension