Abstract:Ti-6Al-4V selective dissolution occurs in vivo on orthopedic implants as the leading edge of a pitting corrosion attack. A gap persists in our fundamental understanding of selective dissolution and pre-clinical tests fail to reproduce this damage. While CoCrMo clinical use decreases, Ti-6Al-4V and the crevice geometries where corrosion can occur remain ubiquitous in implant design. Additionally, most additively manufactured devices cleared by the FDA use Ti-6Al-4V. Accelerated preclinical testing, therefore, would aid in the evaluation of new titanium devices and biomaterials. In this study, using temperature, we (1) developed an accelerated pre-clinical methodology to rapidly induce dissolution and (2) investigated the structure-property relationship between the dissolving surface and the oxide layer. We hypothesized that solution temperature and H2O2 concentration would accelerate oxide degradation, increase corrosion kinetics and decrease experimental times. To assess this effect, we selected temperatures above (45 °C), below (24 °C), and at (37 °C) physiological levels. Then, we acquired electrochemical impedance spectra during active β dissolution, showing significant decreases in oxide polarization resistance (Rp) both over time (p = 0.000) and as temperature increased (p = 0.000). Next, using the impedance response as a guide, we quantified the extent of selective dissolution in scanning electron micrographs. As the temperature increased, the corrosion rate increased in an Arrhenius-dependent manner. Last, we identified three surface classes as the oxide properties changed: undissolved, transition and dissolved. These results indicate a concentration and temperature dependent structure-property relationship between the solution, the protective oxide film, and the substrate alloy. Additionally, we show how supraphysiological temperatures induce structurally similar dissolution to tests run at 37 °C in less experimental time. STATEMENT OF SIGNIFICANCE: Within modular taper junctions of total hip replacement systems, retrieval studies document severe corrosion including Ti-6AL-4V selective dissolution. Current pre-clinical tests and ASTM standards fail to reproduce this damage, preventing accurate screening of titanium-based biomaterials and implant designs. In this study, we induce selective dissolution using accelerated temperatures. Building off previous work, we use electrochemical impedance spectroscopy to rapidly monitor the oxide film during dissolution. We elucidate components of the dissolution mechanism, where oxide degradation precedes pit nucleation within the β phase. Using an Arrhenius approach, we relate these accelerated testing conditions to more physiologically relevant solution concentrations. In total, this study shows the importance of including adverse electrochemical events like cathodic activation and inflammatory species in pre-clinical testing.

Expanded Windows for Titanium Use in the Pulp/Paper Peroxide Bleach Plant

The Corrosion Behavior of Titanium in Hydrogen Peroxide Solution with Various Additives

Corrosion behavior of titanium in hydrogen peroxide solutions

Bioactive treatment of titanium surface using a H2O2/HCl solution

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

Electrochromism of titanium oxide thin films

Electrochemical Corrosion of Titanium and Titanium Alloys Anodized in H2SO4 and H3PO4 Solutions

Electrochemical anodizing treatment to enhance localized corrosion resistance of pure titanium

Influence of Cupric, Ferric, and Chloride on the Corrosion of Titanium in Sulfuric Acid Solutions Up to 85°C

Corrosion Resistance and Ion Dissolution of Titanium Implant under Different Temperature Thermal Oxidation

An insight into the evolution of corrosion resistant coatings on titanium during bipolar plasma electrolytic oxidation in sulfuric acid

Effect of Natural Inhibitors on the Corrosion Properties of Grade 2 Titanium Alloy

Impact of Hydrogen Peroxide and Albumin on the Corrosion Behavior of Titanium Alloy (Ti6Al4V) in Saline Solution

Influence of concentration of sulfuric and hydrochloric acids on corrosion resistance of porous titanium

Corrosion Resistance of Industrial Pure Titanium and its Alloys under High Temperature and Different Cooling Methods

Corrosion Behavior of Titanium Alloys (Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V y Ti Beta-C) with Anodized and Exposed in NaCl and H2SO4 Solutions

Use of Organic Acids as Additives for Plasma Electrolytic Oxidation (PEO) of Titanium

Corrosion of titanium: Part 1: aggressive environments and main forms of degradation

Corrosion protection of highly porous titanium by surface engineering

Increasing temperature accelerates Ti-6Al-4V oxide degradation and selective dissolution: An Arrhenius-based analysis

Benzalkonium chloride/titanium dioxide as an effective corrosion inhibitor for carbon steel in a sulfuric acid solution