High conductivity poly( meta -terphenyl alkylene)s proton exchange membranes for high temperature fuel cell

Xueqing You,Qing Ju,Yichang Ma,Guiqin Yi,Zhangtang Jiang,Nanwen Li,Qiugen Zhang

DOI: https://doi.org/10.1016/j.cej.2024.150535

IF: 15.1

2024-03-23

Chemical Engineering Journal

Abstract:Phosphoric acid (PA)-doped membranes are regarded as a promising candidate for high temperature proton exchange membranes (HT-PEMs), but the trade-off between mechanical property and conductivity is a major problem limiting their application. Here, two poly( meta -terphenyl alkylene)s ( m -TPNs), namely m -TPN-MeIm and m -TPN-TMA, are synthesized by 1-methylimidazole (MeIm) and trimethylamine (TMA) reacting with precursor polymer, respectively. The influence of different cationic groups on the properties of m -TPNs HT-PEMs is investigated in detail. m -TPNs diminish plastication of PA molecules on the mechanical property by separating the adsorption sites for PA molecules from the polymer backbone through long alkyl side chains. As a result, both m -TPN-MeIm and m -TPN-TMA membranes exhibit good mechanical property. Besides, m -TPN-TMA/PA surpasses m -TPN-MeIm/PA in most of aspects owing to the higher ion exchange capacity (IEC) and more distinct microphase separation structure. Noticeably, the proton conductivity of m -TPN-TMA/PA is as high as 0.191 S cm −1 and exhibits excellent stability over a testing time of 100 h at 160 °C thanks to the remarkable acid uptake and microphase separation structure. The m -TPN-TMA/PA-based single cell produces an impressive peak power density of 552 mW cm −2 at 200 °C. Therefore, this work offers a viable alternative for structure design to mitigate the trade-off effect of PA-doped HT-PEMs.

engineering, chemical, environmental