All-Inorganic Perovskite Quantum Dots Based on InX 3 -Trioctylphosphine Oxide Hybrid Passivation Strategies for High-Performance and Full-Colored Light-Emitting Diodes
Yanni Sun,Xikang Yang,Wei Jiao,Jun Wu,Zhenfu Zhao
DOI: https://doi.org/10.1021/acsaelm.0c00951
IF: 4.494
2020-12-28
ACS Applied Electronic Materials
Abstract:All-inorganic perovskite quantum dot (PeQD) light-emitting diodes (QLEDs) are promising candidates for the next-generation flat-panel displays and semiconductor lighting technology. However, the stability issues severely limit their commercial applications. In this study, highly stable CsPbX<sub>3</sub> (X = Cl, Br, I) PeQD films were prepared using InX<sub>3</sub> (X = Cl, Br, I) and trioctylphosphine oxide (TOPO) as inorganic–organic hybrid ligands to passivate the surface defects of PeQDs. The obtained InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs not only have high photoluminance quantum yields (PL QYs) and very narrow emission (14–35 nm) but also possess long-term stability. This is mainly due to the synergistic effect of InX<sub>3</sub> and TOPO inorganic–organic surface ligand passivation, which can effectively inhibit the halogen vacancy and reduce the surface defect of PeQDs. In addition, the chemical states of InBr<sub>3</sub>-TOPO-CsPbBr<sub>3</sub> PeQDs were analyzed by XPS technology and it was found that InX<sub>3</sub>-TOPO synergistic surface passivation can effectively reduce the Pb═O bond in the crystal lattice. Moreover, full-colored perovskite QLEDs based on InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs were achieved by using ZnO/PBD as the double electron transport layer, NiO/TFB as the double hole transport material, and InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs as the light-emitting layer. The EQE (%) and luminance (cd m<sup>–2</sup>) of red, green, and blue QLEDs based on these InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs were 8.2% and 9080 cd m<sup>–2</sup>, 7.8% and 18,600 cd m<sup>–2</sup>, and 1.62% and 164 cd m<sup>–2</sup>, respectively. This cooperative effect based on the InX<sub>3</sub>-TOPO hybrid passivation strategy will open a way for the preparation of highly efficient, stable, and color-tunable perovskite QLEDs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.0c00951?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.0c00951</a>.PL spectrums, PL decay times, and X-ray diffraction (XRD) patterns of pure CsPbBr<sub>3</sub>, InBr<sub>3</sub>-CsPbBr<sub>3</sub>, TOPO-CsPbBr<sub>3</sub>, and InBr<sub>3</sub>-TOPO-CsPbBr<sub>3</sub> PeQDs, respectively; TEM image and size distribution histograms of InBr<sub>3</sub>-TOPO-passivated CsPbBr<sub>3</sub> and unpassivated CsPbBr<sub>3</sub> QDs; SEM images of perovskite quantum dots films at different mole ratios of InBr<sub>3</sub>: TOPO: PbBr<sub>2</sub>; High-resolution XPS of O 1s and CIE color coordinates; SEM morphologies of blue, green, and red InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs films; Cross-section SEM of QLEDs and the stability of InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQD films; PL QYs of InX<sub>3</sub>-TOPO-CsPbX<sub>3</sub> PeQDs; PL decay parameters of pure CsPbBr<sub>3</sub> QDs, TOPO-CsPbBr<sub>3</sub> QDs, InBr<sub>3</sub>-CsPbBr<sub>3</sub> QDs, and InBr<sub>3</sub>-TOPO-CsPbBr<sub>3</sub> QDs; and EL parameters of red, green, and blue InX<sub>3</sub>-TOPO-passivated CsPbX<sub>3</sub> perovskite QLEDs and unpassivated CsPbX<sub>3</sub> QLEDs (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00951/suppl_file/el0c00951_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,engineering, electrical & electronic