The facile preparation and performances of prelithiated silicon oxide anode materials
Chunping Hou,Zeyu Yue,Hehang Sun,Lidong Zhai,Haidong Xie,Hui Tian,Yuqing Qu,Xinwei Wang,Jiao Hou
DOI: https://doi.org/10.1007/s10854-024-12708-z
2024-05-15
Journal of Materials Science Materials in Electronics
Abstract:Silicon oxide (SiO x ) anode materials have gained significant attention in lithium-ion batteries due to their high theoretical specific capacity (above 1965 mAh g −1 ), relatively stable cycling performance, and lower production costs. However, SiO x anode materials tend to form a solid electrolyte interphase (SEI) film and generate inert substances like Li 2 O and Li 4 SiO 4 during the initial charge and discharge processes, leading to the consumption of active lithium ions and low initial coulombic efficiency. To address these issues effectively, prelithiation of SiO x anode materials is explored in this study. A lithium powder suspension is prepared by dispersing lithium powder and carbon nanotubes (CNTs) in the electrolyte, served as the prelithiation agent. The SiO/G@C@A anode material is then prelithiated with this agent. The lithium powder suspension prelithiation agent enables effective prelithiation of the anode material. The SiO@C@A-1 anode exhibits improved electrochemical performances. At a current density of 0.1 A g −1 , the initial specific capacity reaches 981.3 mAh g −1 with an initial coulombic efficiency of 95.65%, which is approximately 25% higher than that of the untreated sample. After 100 cycles and at a current density of 0.5 A g −1 , the prelithiated sample retains a discharge specific capacity of 648 mAh g −1 , with a capacity retention rate of 83.27%, around 10% higher than that of the untreated sample, demonstrating excellent cycling performances.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied