Enhanced Photocatalytic Performance of HTO/TiO2 Composites Prepared by Hydrothermal Soft Chemical Synthesis Under UV Irradiation
Yi‐en Du,Guopeng Wu,Hang Zhou,Zhengyang Li,Juan Li,Zhenwei Zhang
DOI: https://doi.org/10.1002/slct.202400271
2024-08-25
ChemistrySelect
Abstract:White metatitanic acid HTO/TiO2 composites with co‐exposed [111]‐, {010} and {101} facets were successfully synthesized by using delaminated H2TiO3 nanosheets as the precursor via a hydrothermal soft chemical synthesis method in the presence or absence of [Emim]Br, Bmim [Pmim]BF4 ionic liquids. The Bmim‐HTO/TiO2 composite exhibits superior photocatalytic activity for the degradation of MB, which can be attributed to the synergistic effects resulting from its larger specific surface area, the co‐exposure of [111]‐ and {101} facets, a suitable heterojunction structure, and an efficient charge carrier separation. White metatitanic acid H2TiO3 (HTO)/TiO2 composites with co‐exposed [111]‐, {010} and {101} facets were successfully synthesized by employing the white suspension of [TMA+]2[TiO3]2− as the precursor via a hydrothermal soft chemical synthesis method in the presence or absence of 1‐ethyl‐3‐methylimidazolium bromide ([Emim]Br), 4‐bromine imidazole (Bmim) and 1‐methyl‐3‐propylimidazole tetrafluoroborate ([Pmim]BF4) ionic liquids. The structure, morphology, specific surface areas, microstructure, surface properties, and charge migration behaviors of HTO/TiO2 composites vary depending on the selected ionic liquid. The apparent rate constant of the Bmim‐HTO/TiO2 composite was the highest, at 0.0353 min−1, which was approximately 1.35, 1.38, 1.44, 2.67, and 88.25 times higher than that of [Pmim]BF4‐HTO/TiO2 (0.0262 min−1), [Emim]Br‐HTO/TiO2 (0.0256 min−1), No IL‐HTO/TiO2 (0.0245 min−1), CM‐TiO2 (0.0132 min−1) and Blank samples (0.0004 min−1), respectively. Compared with CM‐TiO2 and other HTO/TiO2 samples, the Bmim‐HTO/TiO2 composite featuring cuboid anatase TiO2 nanocrystals with co‐exposed [111]‐facets and {101} facets, exhibited superior photocatalytic activity in degrading methylene blue (MB) under ultraviolet light irradiation. This exceptional performance can be attributed to its cooperative effects, including a larger specific surface area, the co‐exposure of [111]‐ and {101} facets, a suitable heterojunction structure, and the most efficient charge carrier separation. This work introduces a hydrothermal soft chemical process for preparing HTO/TiO2 composite with controllable morphology and co‐exposed reactive facets, which holds promise for practical applications in removing organic pollutants from printing and dyeing wastewater.
chemistry, multidisciplinary