Abstract:The weatherability of weathering steel depends on the protection of the compact rust layers on its surface. However., the compact rust layers might be damaged when they were subject to external actions, for example, collision and scrape etc., which will influence the protective effect on steel base. It is deserved to put attention on further corrosion behavior of the samples with damaged rust layer, which will determine the long term corrosion property. In the present study, electrochemical measurement, metallographic observation and energy disperse spectrum analysis were employed to investigate the further corrosion behaviors of a low carbon bainitic steel in the environment containing Cl-, after its original rust layers had been damaged on different degrees. It was found that the damnification of rust layers on both the low carbon bainitic steel and low carbon steel as a contrast could be rapidly self-repaired in the further corrosion process. When damnification degree and further corrosion time are the same, the resistance and the repair ratio of damaged rust layers on the low carbon bainitic steel are higher than those of the low carbon steel. The fracture toughness of the steel base/rust layer interface of the low carbon bainitic steel is higher than that of the rust layers, so the rust layers would not be abscised thoroughly from the interface and some residual rust would be remained when the steel is subjected to applied actions. The formation of new rust at the damaged sites can be significantly promoted by the residual rust. The contents of Cu and Cr in the original rust layers are close to those in the newly formed rust layers, and both of them are equivalent to those in the steel base. These results indicate that low carbon bainitic steel with excellent mechanical properties and weld ability is a potential candidate for novel weathering steels with higher strength.

Understanding the Structure and Electrochemical Behavior of the Rust Layer Formed on a High-Strength Low-Alloy Structural Steel under Cyclic Exposure to Polluted Marine Atmosphere

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Structure and Electrochemical Behavior of the Rust on 690 MPa Grade Construction Steel in a Simulated Industrial Atmosphere

Influence of Rust Layers on the Corrosion Behavior of Ultra-High Strength Steel 300M Subjected to Wet–Dry Cyclic Environment with Chloride and Low Humidity

Mechanical Performance of Artificially Rusted Q500MC Structural Steel Subjected to High Temperature

Corrosion Behavior of 700L Automotive Beam Steel in Marine Atmospheric Environment

Rust Evolution and Electrochemical Properties of Field-exposed Carbon Steel in a Tropical Marine Environment

Corrosion Behavior of Rusted 550 Mpa Grade Offshore Platform Steel

Corrosion behavior of weathering steel in marine atmosphere

Rust Layer Structure and Corrosion Resistance of High Strength Microalloyed Steels

Rust Layer of Steel Under Various Corrosion Environments

Corrosion Resistance of High Performance Weathering Steel for Bridge Building Applications

Corrosion Behavior of 700 MPa Grade Weathering Steel with 4.0 Wt% Ni and 5.0 Wt% Cr in Simulated Marine Atmospheric Environment

Corrosion behavior of high strength weathering steels in simulated industrial atmosphere environment

EFFECT OF DAMNIFICATION IN RUST LAYER ON CORROSION BEHAVIORS OF LOW CARBON BAINITIC STEEL IN THE ENVIRONMENT CONTAINING Cl-

Corrosion Behavior of New Weathering Steel in the Environment Simulating Coastal Industrial Atmosphere

Corrosion Behaviors and Mechanisms of New Weathering Steel and Carbon Steel in Simulated Industrial Atmosphere

Research on the Rusty Layers of A_3 Carbon Steel and 10crnicup Low-alloy Steel Rusted in Atmospheric Condition

RUSTING EVOLVEMENT OF MILD STEEL UNDER WET/DRY CYCLIC CONDITION WITH Ph 4 NaHSO_3 SOLUTION

ELECTROCHEMICAL STUDY ON RUST OF JT 345 ECONOMICAL WEATHERING STEEL