Abstract:Phosphogypsum (PG) is a solid waste generated during the wet production of phosphoric acid, noted for causing significant environmental pollution due to low pH and contamination with phosphorus-fluorine impurities. This work proposes an innovative method of acid treatment to acidify PG by directly adding of sulfuric acid at suitable temperatures. Initially, this acid treatment process is employed to convert and remove phosphorus-fluorine impurities, followed by PG after acid treatment incorporation with lime for safe solidification. The conversion mechanisms of phosphorus-fluorine impurities during acidification and solidification are elucidated. Results demonstrate that the direct acidification method converts most fluoride into H 2 SiF 6 and HF, which are subsequently released from the PG system after a temperature of 175 °C treatment. Phosphorus is wholly transformed into water-soluble forms (H 3 PO 4 /H 2 PO 4 - /HPO 4 2- ), especially as eutectic phosphorus is released and converted when CaSO 4 ·2 H 2 O crystals dissolve to II-CaSO 4 . Following acidification to achieve a high water-soluble phosphorus/fluorine ratio, lime is added to convert phosphorus-fluorine impurities into Ca 5 (PO 4 ) 3 F, ensuring harmlessness. The addition of 3.7 % lime to acidified PG, an acid amount of 2-times the theoretical requirement, yields a treatment solution with pH=8.65, ρ(P)=0.05 mg/L and ρ(F - )=1.11 mg/L, meeting Class V water discharge standards (GB 3838–2002). The solidified PG filter residue contains the water–soluble ω(P 2 O 5 ) ≤ 0.01 % and ω(F - ) ≤ 0.0061 %, suitable for safe storage. This work indicates that this process can separate phosphorus impurities with lower energy consumption, providing a harmless PG treatment. Furthermore, the treated PG can hydrate to gain strength, potentially enhancing its utility as a resource.

Indirect mineral carbonation of phosphogypsum for CO2 sequestration

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Utilization of Phosphogypsum to Prepare High-Purity CaCO 3 in the NH 4 Cl–NH 4 OH–CO 2 System

Enhanced Carbon Sequestration Via Phosphogypsum Utilization in Conjunction with Concrete Wastewater Treatment

Copper Slag Assisted Coke Reduction of Phosphogypsum for Sulphur Dioxide Preparation

Preparation of calcium carbonate by indirect carbonation desulfurization gypsum with renewable aspartic acid

Procedure to use phosphogypsum industrial waste for mineral CO2 sequestration

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Preparation of Calcium Oxide by Decomposition of Phosphogypsum under CO and Water Vapor Atmosphere

Unlocking high carbonation efficiency: Direct CO2 mineralization with fly ash and seawater

Enhancing the Performance of Hemihydrate Phosphogypsum by the Collaborative Effects of Calcium Hydroxide and Carbonation

Carbon sequestration through mineral carbonation: Using commercial FGD-gypsum from a copper smelter for sustainable waste management and environmental impact mitigation

Preparation of gypsum with high purity and whiteness from phosphogypsum for CO2 mineral sequestration

In-situ remediation of phosphogypsum in a cement-free pathway: Utilization of ground granulated blast furnace slag and NaOH pretreatment

Effect of MgO and superfine slag modification on the carbonation resistance of phosphogypsum-based cementitious materials: Based on hydration enhancement and phase evolution regulation

Carbonated ground granulated blast furnace slag stabilising brown kaolin

Research on the technology and mechanism of direct acidification of phosphogypsum and deeply solidify impurities with lime

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum

Preparation of α-hemihydrate gypsum from phosphogypsum in recycling CaCl2 solution

Recyclable and Efficient Recovery of Ca and S from Phosphogypsum by Using Multistep Precipitation

Indirect mineralization of CO 2 using recyclable glycine with carbide slag