Abstract:Melt-blown nonwoven fabrics for filtration are usually manufactured using polypropylene, but after a certain time period the middle layer of the mask may have a reduced effect on adsorbing particles and may not be easily stored. Adding electret materials not only increases storage time, but also shows in this study that the addition of electret can improve filtration efficiency. Therefore, this experiment uses a melt-blown method to prepare a nonwoven layer, and adds MMT, CNT, and TiO2 electret materials to it for experiments. Polypropylene (PP) chip, montmorillonite (MMT) and titanium dioxide (TiO2) powders, and carbon nanotube (CNT) are blended and made into compound masterbatch pellets using a single-screw extruder. The resulting compound pellets thus contain different combinations of PP, MMT, TiO2, and CNT. Next, a hot pressor is used to make the compound chips into a high-poly film, which is then measured with differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR). The optimal parameters are yielded and employed to form the PP/MMT/TiO2 nonwoven fabrics and PP/MMT/CNT nonwoven fabrics. The basis weight, thickness, diameter, pore size, fiber covering ratio, air permeability, and tensile property of different nonwoven fabrics are evaluated in order to have the optimal group of PP-based melt-blown nonwoven fabrics. According to the results of DSC and FTIR measurements, PP and MMT, CNT, and TiO2 are completely mixed, and the melting temperature (Tm), crystallization temperature (Tc) and endotherm area are changed accordingly. The difference in enthalpy of melting changes the crystallization of PP pellets, which in turn changes the fibers. Moreover, the Fourier transform infrared (FTIR) spectroscopy results substantiate that PP pellets are well blended with CNT and MMT, according to the comparisons of characteristic peaks. Finally, the scanning electron microscopy (SEM) observation suggests that with a spinning die temperature of 240 °C and a spinning die pressure lower than 0.01 MPa, the compound pellets can be successfully formed into melt-blown nonwoven fabrics with a 10-micrometer diameter. The proposed melt-blown nonwoven fabrics can be processed with electret to form long-lasting electret melt-blown nonwoven filters.

Design of Polypropylene Electret Melt Blown Nonwovens with Superior Filtration Efficiency Stability through Thermally Stimulated Charging

Water electret charging based polypropylene/electret masterbatch composite melt-blown nonwovens with enhanced charge stability for efficient air filtration

Light stabilizer-modified hydrocharging melt-blown nonwovens with superior charge stability for air filtration

Multi-Layered, Corona Charged Melt Blown Nonwovens as High Performance PM0.3 Air Filters

High Filterable Electrospun Nanofibrous Membrane with Charged Electret After Electrification Treatment for Air Filtration

Research on Polypropylene Electret Melt-Blown Nonwoven Doped with Nano-Tourmaline

High-performance Electret and Antibacterial Polypropylene Meltblown Nonwoven Materials Doped with Boehmite and ZnO Nanoparticles for Air Filtration

Design of electret polypropylene melt blown air filtration material containing nucleating agent for effective PM2.5 capture

Long-Lasting Electret Melt-Blown Nonwoven Functional Filters Made of Organic/Inorganixc Macromolecular Micron Materials: Manufacturing Techniques and Property Evaluations

Simulation and experimental investigation of electret polypropylene fiber preparation via centrifugal melt electrospinning for enhanced air filtration

Trap-induced hydro-charging polylactic acid nonwovens with high charge storage capability for stable and efficient air filtration

Bicomponent spunbond filters doped with polytetrafluoroethylene nanoparticles for long-term efficient fine particle removal

Performance optimization of electret air filter

Bioelectrets in Electrospun Bimodal Poly(lactic Acid) Fibers: Realization of Multiple Mechanisms for Efficient and Long-Term Filtration of Fine PMs.

Electret Nonwoven Structures for High-Efficiency Air Filtration, Produced Using the Blow Spinning Technique

Polypropylene/Polyvinyl Alcohol/Metal-Organic Framework-Based Melt-Blown Electrospun Composite Membranes for Highly Efficient Filtration of PM2.5

Preparation of PVA/PEI/CNC/ZnO composite membrane with good mechanical properties and water resistance by electrostatic spinning using for efficient filtration of PM2.5

High Filtration Efficiency Fluffy Material: Nano-Fiber Constructing Gradient Structure on Recycled Curved PET Micro-Fibers Web

The Charge Storage and Its Stability in Corona Charged Polypropylene Non-Woven Fabrics Used As Air Filters

Polylactic Acid/Calcium Stearate Hydrocharging Melt-Blown Nonwoven Fabrics for Respirator Applications

Preparation of Aligned Stereocomplexed Poly(lactic Acid)nanofibrous Membranes for Long-term Electret and Efficient PM0.3 Filtration