Tension–tension fatigue behavior of unidirectional single-walled carbon nanotube reinforced epoxy composite

Yu Ren, Feng Li, Hui-Ming Cheng, Kin Liao

2003-01-01

Abstract:Owing to the recent rapid development of synthesis of about 40 mm in length and 3.5 mm in width were cut methods for carbon nanotubes (CNTs), high quality, long from the cured thin composite plate, and their edges were and aligned CNT ropes are now available [1–5]. These polished to reduce the possibility of edge-related failures advances in synthesis methods enabled the mechanical(Fig. 1). The volume fraction of SWNT ropes in the properties of CNTs to be more easily assessed, and composite was controlled within the range 0.1–0.9%. Nine applications in macroscopic devices and load-bearing unidirectional SWNT/epoxy specimens with gauge length structures one step closer to reality. To date, some of the of about 15 mm were fabricated and cyclically tested by an most important mechanical properties of CNTs, such as the Instron 8800 Microforce Tester in under tension–tension Young’s modulus and tensile strength, have been char- at 5 Hz, using a sinusoidal wave function at an R ratio acterized experimentally [6–10]. At present, however,(ratio of minimum to maximum cyclic stress) of 0.1. studies on the long-term performance of CNTs or CNT Since the SWNT volume fraction varied from sample to reinforced composites are still absent. An understanding of sample, on an S–N plot SWNT stress cannot be inferred their behavior under repeated mechanical loads will enable from the applied stress of the composite according to the the potential of CNTs to be better realized for long-term rule of mixtures. Therefore, the maximum cyclic SWNT structural applications. In this study, the fatigue behavior stress is plotted against the number of …