Dendrite-free solid-state lithium batteries enabled by fluorine doped Li7La3Zr2O12 composite electrolyte and LiAlF4 Interphase

Yuezhen Mao,Fanghui Mi,Tianyuan Wang,Zhijun Zhang,Chunwen Sun

DOI: https://doi.org/10.1039/d4qi01111b

IF: 7.779

2024-06-14

Inorganic Chemistry Frontiers

Abstract:Solid-state lithium metal batteries (SSLMBs) have gained much interest owing to the advantages of high specific energy density and safety performance. Nevertheless, the low ionic conductivity of the solid electrolyte and poor contact between lithium metal and electrolyte have hindered their widespread application. In this work, fluorine doped Li7La3Zr2O12 (LLZOFx) was used to improve the ionic conductivity of the composite electrolyte, and then AlF3 was employed to construct a lithophilic layer on the surface of lithium anode, which can effectively improve the conformity of electrolyte and lithium metal. The LLZOF0.2 CSE exhibits not only high ionic conductivity of 3.9×10-4 S cm-1 but also a wide electrochemical window of 5.44 V and an improved Li+ transference number of 0.61. Furthermore, the adsorption and binding energies of LLZOF0.2 on lithium bis(trifluoromethanesulfonyl)imide (LITFSI) were determined through calculations. The results indicate that LLZOF0.2 can reduce the binding energy of LiTFSI, and adsorb TFSI-, therefore increase the amount of free lithium ions. In addition, a lithophilic layer was constructed on the surface of the lithium metal. This layer composed of LiF and LiAlF4 effectively reduces interfacial resistance, lowers the overpotential of the symmetric cell, and inhibits the growth of dendrites. The experimental results indicate that the cell composed of LLZOF0.2 based CSE and Li@AlF3 demonstrates outstanding electrochemical performance. The capacity retention rate of the cell with LLZOF0.2 based CSE and LiAlF4 interphase is 86.9% after 300 cycles at 1C.

chemistry, inorganic & nuclear