Fabrication of MOF-derived tubular In2O3@SnIn4S8 hybrid: Heterojunction formation and promoted photocatalytic reduction of Cr(VI) under visible light

Meng Sun,Fengli Li,Mingjian Su,Dong Wei,Qianqian Yang,Tao Yan,Danzhen Li

DOI: https://doi.org/10.1016/j.jcis.2021.02.121

IF: 9.9

2021-08-01

Journal of Colloid and Interface Science

Abstract:Tubular In₂O₃@SnIn₄S₈ hierarchical hybrid photocatalyst was firstly fabricated by a two-step method. The morphology and composition were characterized by scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). The XRD results show that the obtained In₂O₃ microtubes were highly crystallized, while the SnIn₄S₈ flakes prepared at low temperature were poorly crystallized. The SEM image of the hybrid shows that numerous SnIn₄S₈ nanoflakes were assembled over the surface of In₂O₃ microtubes. In₂O₃ served as dispersing-templates have reduced the agglomeration of SnIn₄S₈ flakes. Meanwhile, the heterojunctions formed at the interfaces between In₂O₃ and SnIn₄S₈ could facilitate the interfacial charge transfer, as well as promote the photocatalytic activity of the hybrid. In the treatment of Cr(VI)-containing wastewater, the In₂O₃@SnIn₄S₈ hybrid not only exhibited strong adsorption ability, but also showed remarkably enhanced photocatalytic activity compared with pure SnIn₄S₈. The photocatalytic reaction constant k for In₂O₃@SnIn₄S₈ was approximately 2.54 times higher than that of SnIn₄S₈. The efficient activity of this hybrid photocatalyst should be ascribed to the promoted separation efficiency of electron/hole pairs, which was proved by the following three-dimensional excitation-emission matrix fluorescence spectra (3D EEMs), photocurrent responds, and EIS characterizations.

chemistry, physical