Abstract:Failure response of the modern high strength steel grades shows a diverse pattern compared to the conventional highly ductile steels. In automotive sheet forming applications of the high strength steels, fracture could be observed prior to necking or the post necking deformation is very limited. The differences in the underlying damage mechanisms contribute to the different ways of damage development and the interaction of damage with plastic localization and strain hardening creates various failure patterns. Therefore, it is critical to clearly identify the phase for damage initiation and understand the relation between plastic localization, damage and fracture, as these patterns significantly influence the safety assessment in the forming process of steels. Inverse modelling approaches are being used to bridge the gap between experiments and numerical simulations. However, this technique shows significant discrepancies when strain heterogeneity is experienced, especially since the determination of the material parameters is based on comparison on a global scale with force and elongation measurements. An iterative finite element model update (FEMU) procedure integrated with optical full field measurement technique was executed which extended the possibilities to identify the material ductile damage and fracture behavior on a local level with significantly higher accuracy. To identify the material plastic and damage behavior of the automotive dual phase steel (DP-K1000) under study, experiments are conducted on dog-bone, notched tensile, central hole and shear specimens at various strain rates. Full field deformation data was obtained by digital image correlation (DIC). A vigorous and general framework for the inverse identification of the strain hardening behavior up to fracture of the automotive high strength steel was studied. A hybrid damage mechanics model (extended Modified Bai-Wierzbicki) that combines a phenomenological criterion for damage initiation related to the microstructure degradation of materials and a continuum damage mechanics based damage evolution law for progressive damage accumulation till final fracture is employed using a VUMAT in the finite element (FE) scheme. To exclude the convergence (plastic instability) problems, a displacement driven finite element simulation was used while minimizing the discrepancy between the experimental and numerical surface strain fields and force values. A visual mapping procedure was adopted to realize identical reference frames and therefore identical peripheries for the specimen in DIC and FE model. This mapping includes a transformation and interpolation function from FE results to the DIC datum points. Successful identification of the material parameters was achieved based on a combined Gauss-Newton and Levenberg-Marquardt algorithm which require the evaluation of the gradient of the objective function to update the unknown parameters in an appropriate direction. The optimization problem of the inverse modelling in the current work was described by a cost function based on the least square norm of the differences of the surface strain fields. Overall cost function formulation is not dependent on the experimental or finite element meshes and includes rigid body motions. The residual was minimized at once for all the displacements by Gauss-Newton scheme in space-time, which is defined by spatial domain and temporal domain. The optimization of the constitutive parameters was directly achieved by minimizing this image residual in an iterative manner. The adopted methodology helped in determining macroscopic crack initiation instant and location from experiments. Local variables such as equivalent plastic strain, stress triaxiality and Lode angle parameter were evaluated from the critical element for the determination of the damage initiation locus which was then fitted by a non-linear least squares method with a trust-region algorithm in Matlab. The identified damage initiation locus and plastic localization phenomena served as an evaluation criteria for the formability of the dual phase automotive steel.

Localized heat treatment and XFEM-based investigation of damage mechanisms in reinforced notched plates under uniaxial tensile stress

Damage analysis of Functionally Graded Materials under strong cyclic loading

Numerical and experimental analysis of the notch effect on fatigue behavior of polymethylmethacrylate metal based on strain energy density method and the extended finite element method

Using FGM concept in fiber-matrix coupling laws to predict the damage in carbon-Epoxy graded composite application in notched plate under thermo-mechanical loading

Revealing plastic localization and ductile damage initiation features with integrated DIC and FEM

Experimental and Computational Study of Microstructural Effect on Ductile Fracture of Hot-Forming Materials

Development of a non-local approach for life prediction of notched specimen considering stress/strain gradient and elastic-plastic fatigue damage

Effect of elliptical notches on mechanical response and progressive damage of FMLs under tensile loading

A Novel Damage Model To Predict Ductile Fracture Behavior For Anisotropic Sheet Metal

Modeling of the ductile damage – Application for bar shearing

A Coupled XFEM Fatigue Modelling of Crack Growth, Delamination and Bridging in FRP Strengthened Metallic Plates

Fracture mechanics approach to fatigue crack initiation at uniaxially loaded notches

Numerical analysis of the elastic-plastic behavior of a tubular structure in FGM under pressure and defect presence

An innovation in finite element simulation via crystal plasticity assessment of grain morphology effect on sheet metal formability

Block structured adaptive mesh refinement and strong form elasticity approach to phase field fracture with applications to delamination, crack branching and crack deflection

A New Approach To Damage Modelling And Fracture Analysis For Metal Bar With V-Shaped Notch

Nonlocal modeling in high-velocity impact failure of 6061-T6 aluminum

Numerical Modeling for Hole-Edge Cracking of Advanced High-Strength Steels (AHSS) Components in the Static Bend Test

Experimental analysis of strain path dependent ductile damage mechanics and forming limits

Effect of Notch Radius on Anisotropic Fracture Response of AA6061-T6 under Tension Process

Broad Stress Triaxiality Ratio Band Fracture Experiments in DP900 Metal Sheets and Corresponding Predictive Capability of Advanced Phenomenological and Micromechanical Fully Coupled Damage Models