Co/MoC Nanoparticles Embedded in Carbon Nanoboxes as Robust Trifunctional Electrocatalysts for a Zn–Air Battery and Water Electrocatalysis
Lei Zhang,Yuanxin Zhu,Zhicheng Nie,Ziyao Li,Ying Ye,Luhan Li,Jie Hong,Zenghui Bi,Yingtang Zhou,Guangzhi Hu
DOI: https://doi.org/10.1021/acsnano.1c03766
IF: 17.1
2021-08-04
ACS Nano
Abstract:To meet the application needs of rechargeable Zn–air battery and electrocatalytic overall water splitting (EOWS), developing high-efficiency, cost-effective, and durable trifunctional catalysts for the hydrogen evolution reaction (HER), oxygen evolution, and reduction reaction (OER and ORR) is extremely paramount yet challenging. Herein, the interface engineering concept and nanoscale hollowing design were proposed to fabricate N-doping carbon nanoboxes confined with Co/MoC nanoparticles. Uniform zeolitic imidazolate framework nanocube was employed as the starting material to construct the trifunctional electrocatalyst through the conformal polydopamine–Mo layer coating and the subsequent pyrolysis treatment. The / catalyst displayed superior electrochemical ORR performances with a positive half-wave potential of 0.875 V and a high limiting current density of 5.89 mA/cm2. When practically employed as an electrocatalyst in regenerative Zn–air battery, a high specific capacity of 728 mAh/g, a large peak power density of 221 mW/cm2, a high open-circuit voltage of 1.482 V, and a low charge/discharge voltage gap of 0.41 V were obtained. Moreover, its practicability was further exploited by overall water splitting, affording low overpotentials of 277 and 68 mV at 10 mA/cm2 for the OER and HER in 1 M KOH solution, respectively, and a decent operating potential of 1.57 V for EOWS. Ultraviolet photoelectron spectroscopy and density functional theory calculation revealed that the Co/MoC interface synergistically facilitated the charge-transfer, thereby contributing to the enhancements of electrocatalytic ORR/OER/HER processes. More importantly, this catalyst design concept can offer some interesting prospects for the construction of outstanding trifunctional catalysts toward various energy conversion and storage devices.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsnano.1c03766.Experimental section; XRD patterns, photographs, EDS spectra, SEM and TEM images of different precursors; Raman and XPS spectra of various catalysts; schematic model; partial density of states and total density of states; ORR and OER polarization curves; methanol crossover tolerance for ORR; durability evaluation curves; digital image of the Zn–air button battery; reduction peaks; linear fitting; amounts of H2 and O2 experimentally measured and theoretically calculated; SEM images and HRXPS spectra after OER and HER; summaries of electrochemical performances (PDF)Movie S1 of HER performance of / product (MP4)Movie S2 of OER performance of / product (MP4)Movie S3 of EOWS performance of / product (MP4)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology