Abstract:The thermal stabilization process of polyacrylonitrile (PAN) precursor fiber was the key step to prepare high-performance carbon fiber. During the thermal stabilization process, the aggregation structure and the reactivity of molecular chains have significant effects on the microstructures and mechanical properties of carbon fiber. In the present paper, the effects of the orientation structure of PAN precursor fiber on the thermal stabilization reaction and the mechanical properties of carbon fiber were experimentally studied. Using multi-dimensional structural and mechanical properties tests, such as XRD, DSC, 13C NMR and Instron machine testing, the crystalline and skeleton structure, exothermic behavior, and tensile properties of PAN precursor fiber with different orientations in the process of thermal stabilization were characterized to reveal the relationship between microstructure evolution and tensile properties. The results showed that the orientation structure of PAN precursor fiber had an obvious effect on the thermal stabilization process and the tensile stress–strain characteristic. When the heat treatment temperature was lower than 200 °C, the crystallinity and crystallite size of PAN fibers with higher orientation degrees increased significantly. After sufficient thermal stabilization, the original PAN precursor fiber with a higher orientation degree could form more aromatic lamellar structures and showed better regularity. Furthermore, the yield strength and initial modulus of the fibers with a higher orientation degree increased due to the formation of more aromatic rings. The maximum increase in the percentages of yield strength and tensile modulus of the PAN fibers were achieved when the heat-treated temperature was 200 °C, and the percentage values were 138.4% and 158.7% compared to the precursor without heat-treatment. In addition, the elongation at break of the fibers with a higher orientation degree was also relatively larger.

One kind of a large diameter high strength and high modulus PAN-based carbon fiber and its preparation method

In-situ doping B4C nanoparticles in PAN precursors for preparing high modulus PAN-based carbon fibers with boron catalytic graphitization

2D-Topology-seeded Graphitization for Highly Thermally Conductive Carbon Fibers

Two‐dimensional Topology‐Seeded Graphitization for Highly Thermally Conductive Carbon Fibers

Carbon Welding by Ultrafast Joule Heating.

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Polyacrylonitrile sheath and polyacrylonitrile/lignin core bi-component carbon fiber

Enhanced both in-plane and through-thickness thermal conductivity of carbon fiber/epoxy composites by fabricating high thermal conductive coaxial PAN/PBO carbon fibers

Graphene Interlocking Carbon Nanotubes for High-Strength and High-Conductivity Fibers.

Method for preparing polyacrylonitrile-based porous hollow carbon fibers by coaxial electrospinning

Preparation method of flexible porous carbon fiber

Structural Features of Polyacrylonitrile-Based Carbon Fibers

A one-step hot pressing molding method of polyacrylonitrile carbon fibers: influence on surface morphology, microstructure and mechanical property

Large-scale preparation of thermally conductive graphene fiber filaments

STUDY ON CARBONIZATION TECHNOLOGY OF LARGE-TOW POLYACRYLONITRIL-BASED PREOXIDIZED FIBER

Preparation and Characterization of Large Diameter Pitchbased Carbon Fiber/abs Resin Composites with High Thermal Conductivities

High-Strength Carbon Nanotube Fibers from Purity Control by Atomized Catalytic Pyrolysis and Alignment Improvement by Continuous Large Prestraining

Effect of the polyacrylonitrile mass fraction on the structure of coaxial polyacrylonitrile/mesophase pitch composite fibers

Effect of Polyacrylonitrile Precursor Orientation on the Structures and Properties of Thermally Stabilized Carbon Fiber

Modification of large tow textile grade polyacrylonitrile fiber by dopamine hydrochloride to prepare low-cost carbon fibers

Mesophase pitch raw material used for preparing high-modulus high-thermal-conductivity carbon fiber, and preparation method thereof