Abstract:<p>A spinodal decomposition is often carried out in the austenite-ferrite duplex stainless steel Fe20Cr9Ni during long-term service at a temperature in the range from 280 to 320°C, resulting in a decrease of pitting corrosion resistance. Fe-rich α phase rather than G-phase has been suggested as the major reason for the deterioration in pitting corrosion resistance of the thermally-aged steel. Here, we found that ∼76.8% of the decline in pitting resistance for the duplex stainless steel Fe20Cr9Ni was attributed to G-phase, and ∼23.2% to Fe-rich α phase after the spinodal decomposition. In this study, a suitable thermal aging treatment was introduced to obtain a larger size of the G-phase and to study the role of the phase in the corrosion process. Through immersing thermally-aged TEM specimen treated at 475°C for 3000 h in NaCl solution, the preferential position of corrosion pits formed in the ferrite was obtained. The composition changes and strain field distribution around the G-phase were analyzed by TEM-EDS, 3DAPT and GPA techniques. We further found that, although the concentration difference of Cr element between α and α' phases was as high as 60 at.%, corrosion pits were initiated at the interface between the G-phase and the ferrite matrix rather than in the Fe-rich α phase, indicating that the Cr-depleted theory could not explain the aforesaid phenomenon. The strain energy at the interface between the G-phase and the ferrite matrix was found to be the largest. The atoms at the interface have higher energy than in the intracrystalline, and thus easily react with Cl<sup>−</sup> ions in the solution to form pits finally.</p>
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: **Evaluate the pitting corrosion behavior of duplex stainless steel Fe20Cr9Ni in nuclear power applications, and study the influence mechanism of G - phase and α - phase (iron - rich phase) on pitting corrosion performance during the thermal aging process**.
### Specific problem decomposition:
1. **Influence of thermal aging on pitting corrosion performance**:
Thermal aging can lead to intergranular decomposition (spinodal decomposition) of duplex stainless steel Fe20Cr9Ni in the temperature range of 280 - 320 °C, thereby reducing its pitting corrosion resistance. The paper attempts to quantify the contribution ratios of G - phase and α - phase to the decline in pitting performance respectively.
2. **Research on the pitting initiation location**:
The paper experimentally verifies whether pitting preferentially occurs in G - phase, α - phase or the matrix, and explores the specific mechanism of action.
3. **Influence of chemical composition and strain field distribution**:
Analyze the chemical composition changes and strain field distribution around G - phase through TEM - EDS, 3DAPT and GPA techniques to reveal the microscopic mechanism of pitting initiation.
---
### Main research objectives:
1. **Quantify the influence of G - phase and α - phase**:
The paper finds that approximately 76.8% of the decline in pitting resistance is attributed to G - phase, and approximately 23.2% is attributed to α - phase.
2. **Pitting initiation mechanism**:
Experiments show that although the Cr concentration difference between α - phase and α' - phase is as high as 60 at.%, pitting preferentially occurs at the interface between G - phase and the ferrite matrix, rather than in α - phase. This indicates that the traditional "Cr - depletion theory" cannot fully explain this phenomenon.
3. **Role of strain energy**:
The strain energy at the interface between G - phase and the ferrite matrix is the largest, resulting in a higher atomic energy in this area, which is prone to react with Cl⁻ ions in the solution to form pitting.
---
### Key formulas involved (assuming relevant calculations exist):
1. **Change in pitting potential**:
$$
\Delta E_{pit} = E_{pit, \text{as - recieved}} - E_{pit, \text{aged}}
$$
where, $E_{pit, \text{as - recieved}} = 418.9 \, \text{mV SCE}$, $E_{pit, \text{aged}} = 132.8 \, \text{mV SCE}$.
2. **Contribution ratios of G - phase and α - phase**:
$$
\text{G - phase contribution ratio} = \frac{\Delta E_{pit, \text{G - phase}}}{\Delta E_{pit}} \times 100\%
$$
$$
\text{α - phase contribution ratio} = \frac{\Delta E_{pit, \text{α - phase}}}{\Delta E_{pit}} \times 100\%
$$
3. **Cr concentration difference**:
$$
\Delta Cr = Cr_{\text{α'}} - Cr_{\text{α}}
$$
where, $Cr_{\text{α'}} = 73 \, \text{at.%}$, $Cr_{\text{α}} = 13 \, \text{at.%}$.
---
### Summary:
The core problem of the paper is to study the pitting corrosion behavior of duplex stainless steel Fe20Cr9Ni during the thermal aging process, especially the influence mechanism of G - phase and α - phase on pitting performance. Through experiments and analysis, the paper reveals that pitting preferentially occurs at the interface between G - phase and the ferrite matrix, rather than in the traditional Cr - depleted regions (such as α - phase). This finding provides new ideas for improving the corrosion resistance of duplex stainless steel.