Abstract:This work aimed to evaluate the effect of niobium addition on nickel-based catalysts and their performance in dry reforming reactions to produce syngas (H 2 and CO). Different quantities of Nb 2 O 5 (5, 10, and 20% w/w) were used to prepare the catalysts, while a fixed content of Ni was applied (20%). The catalysts were supported on MCM-41. Physical, chemical, and morphological analyses were conducted to assess the characteristics of the materials. The produced Nb-Ni catalysts were applied in dry reforming reactions at 800 °C for 12 h. The dry reforming results indicated that the catalyst with 10% Nb-Ni demonstrated the best conversion of CH 4 and CO 2 (> 97%) and a significant H 2 production (40%), with good stability during 12 h of reaction, while the catalyst with 5% Nb-Ni showed lower conversions and did not present good stability during the reaction. The catalyst with 5% Nb-Ni exhibited the highest production of H 2 (44%), and the lowest of CO (50.87%), probably due to the presence of parallel reactions that increased H 2 content and caused carbon (coke) formation. The characterization results of this material revealed the greatest formation of carbon on its surface. The presence of coke can prejudice the efficiency of the catalyst during a reaction and significantly reduce its lifetime. The catalyst with 10% Nb-Ni did not present coke formation, while the catalyst with 20% Nb-Ni showed carbon presence. The good dispersion of Ni on supports (Nb 2 O 5 and SiO 2 /MCM-41) can explain the best behavior of 10% Nb-Ni for dry reforming reactions. X-ray diffractometry of the solids suggests the contribution of both metals (Ni and Nb) to the reforming process. From the obtained results, the catalyst with 10% Nb-Ni was indicated as the most favorable for dry reforming reactions among the studied materials, displaying good stability and conversion along with resistance to carbon formation.

Ni supported on desilicated HZSM-5 as catalyst for biogas reforming

Nickel‐Catalyzed Dry Reforming of Methane Via Modulating the Zirconia Shapes

Study on CO2 reforming of methane to syngas over Al 2O3-ZrO2 supported Ni catalysts prepared via a direct sol-gel process

Performance Study of Ni/Si-MCM-41 Catalysts, Synthesized with Different Silica Sources, and their Application on Methane Dry Reform to Produce Green Hydrogen

Effect of niobium addition over Ni/MCM-41 catalysts for dry reforming of biogas

Combined Catalytic Partial Oxidation and CO2 Reforming of Methane over ZrO2-modified Ni/SiO2 Catalysts Using Fluidized-Bed Reactor

Synthesis, Characterization and Catalytic Performance of MgO-coated Ni/SBA-15 Catalysts for Methane Dry Reforming to Syngas and Hydrogen

Dry reforming of methane over Ni catalysts supported on micro- and mesoporous silica

Syngas production from methane dry reforming over Ni/Al2O3 catalyst

Methane Dry Reforming by Ni–Cu Nanoalloys Anchored on Periclase-Phase MgAlO x Nanosheets for Enhanced Syngas Production

Overcoming the kinetic and deactivation limitations of Ni catalyst by alloying it with Zn for the dry reforming of methane

Syngas Production from Reforming of Methane with Co2 and O-2 over Ni/Sro-Sio2 Catalysts in A Fluidized Bed Reactor

Balance effect between Ni dispersion and hydrophobicity in CO 2 methanation over Ni/ZSM-5

Catalytic conversion of methane and CO2 to synthesis gas over a La2O3-modified SiO2 supported Ni catalyst in fluidized-bed reactor

Bi-reforming of Methane with Carbon Dioxide and Steam on Nickel-Supported Binary Mg–Al Metal Oxide Catalysts

Impact of preparation method on nickel speciation and methane dry reforming performance of Ni/SiO2 catalysts

Ni/SiO<sub>2</sub>Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO<sub>2</sub>Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation

Two-Step, Oxygen-Free Conversion of Methane over Supported NiB Amorphous Alloy Catalysts

Design Dual Confinement Ni@S-1@SiO2 Catalyst with Enhanced Carbon Resistance for Methane Dry Reforming

Highly Active and Stable Ni/ZrO2 Catalyst for Syngas Production by CO2 Reforming of Methane

Design Dual Confinement Ni@S-1@SiO2 2 Catalyst with Enhanced Carbon Resistance for Methane Dry Reforming