The Deterioration of C-S-H Gel in a Severe Sulfate Environment

Wei Liao,Chunhua Lu,Zhongzi Xu

DOI: https://doi.org/10.3390/sym16060703

2024-06-07

Symmetry

Abstract:Immersion tests with 5 wt.% Na2SO4 solution were carried out to investigate the deterioration of calcium silicate hydrate (C-S-H) gel in a sulfate environment. C-S-H gels with different Ca/(Si + Al) molar ratios were used for comparison. Particular attention was paid to the changes in element composition and Si-O-Si chain structure of the C-S-H gel. The results show that the C-S-H gels with a low Ca/(Si + Al) ratio (0.8–1.0) and appropriate Si-O-Si chain length (14.8) presented better stability in a severe sulfate environment. The C-S-H gels with a higher Ca/(Si + Al) ratio (>2.0) were more sensitive to the attack of sulfate ions. Calcium ions dissolved rapidly during the immersion process, causing the loss of cohesive strength of the C-S-H gel, and then decomposed into fine particles. The C-S-H gel with a lower Ca/(Si + Al) ratio (about 1.1) rarely leached out calcium ions and maintained good micromorphology. The 29Si MAS-NMR results indicate that the Si-O-Si chains with too short or too long chain lengths will break and recombine under the attack of sulfate ions. The Si-O-Si chains with an appropriate chain length (14.8) maintained the stability of the structure of the C-S-H gel in a sulfate environment. These changes are closely related to the asymmetric layered structure of amorphous C-S-H gel. Partial calcium ions between the layers of the main chain structure of Si-O-Si are easily taken away by sulfate ions, leading to the structural instability of the C-S-H gel.

multidisciplinary sciences

What problem does this paper attempt to address?

The paper primarily explores the degradation of calcium silicate hydrate (C-S-H) gel in a sulfate environment. Specifically, the study focuses on the stability of C-S-H gels with different Ca/(Si + Al) molar ratios in a 5 wt.% Na₂SO₄ solution. The research investigates C-S-H gels of various compositions through immersion tests, with particular attention to changes in elemental composition and the Si-O-Si chain structure within the C-S-H gel. The study finds that in a sulfate environment, C-S-H gels with lower Ca/(Si + Al) ratios (approximately 0.8-1.0) and appropriate Si-O-Si chain lengths (around 14.8) exhibit better stability. In contrast, C-S-H gels with higher Ca/(Si + Al) ratios (greater than 2.0) are more sensitive to sulfate ion attack, leading to rapid dissolution of calcium ions, which in turn causes the C-S-H gel to lose cohesion and decompose into fine particles. Additionally, the research points out that shorter or excessively long Si-O-Si chains within the C-S-H gel tend to break and reorganize under sulfate ion attack, whereas Si-O-Si chains of appropriate length (about 14.8) can maintain structural stability in a sulfate environment. These changes are closely related to the asymmetric layered structure of amorphous C-S-H gel. In summary, this study aims to understand the behavior characteristics of C-S-H gel under sulfate attack, which is of significant reference value for improving the sulfate resistance of concrete.

The Deterioration of C-S-H Gel in a Severe Sulfate Environment

Effect of Calcium to Silicon Ratio on the Microstructure of Hydrated Calcium Silicate Gels Prepared under Medium Alkalinity

Effect of Corrosive Ions (cl − , SO 4 2− , and Mg 2+ ) on the Nanostructure and Chloride Binding Property of C-A-S-H Gel

Effect of Corrosive Ions (cl−, SO42−, and Mg2+) on the Nanostructure and Chloride Binding Property of C-A-S-H Gel

Microstructural Evolution Mechanism of C-(A)-S-H Gel in Portland Cement Pastes Affected by Sulfate Ions

Hydrated Calcium Silicate Erosion in Sulfate Environments a Molecular Dynamics Simulation Study

Structural evolution of calcium sodium aluminosilicate hydrate (C-(N-)A-S-H) gels induced by water exposure: The impact of Na leaching

Thermodynamic Stability of Sulfate Ions on Calcium Aluminosilicate Hydrate Microstructure

Effects of Sodium Ions on Synthesized Alkali Silica Reaction Gels

Multi-scale investigation on composition-structure of C-(A)-S-H with different Al/Si ratios under attack of decalcification action

Intrinsic Sulfuric Acid Resistance of C-(N)-A-S-H and N-A-S-H Gels Produced by Alkali-Activation of Synthetic Calcium Aluminosilicate Precursors

Effects of pH on the nano/micro structure of calcium silicate hydrate (C-S-H) under sulfate attack

Degradation of C–S–H(I) at different decalcification degrees

Molecular Dynamics Simulation of C-S-H Corrosion in Chloride Environment

Ionic Hydration Structure, Dynamics and Adsorption Mechanism of Sulfate and Sodium Ions in the Surface of Calcium Silicate Hydrate Gel: A Molecular Dynamics Study

Full process of calcium silicate hydrate decalcification: Molecular structure, dynamics, and mechanical properties

Microstructural evolution and degradation mechanisms of tricalcium silicate and tricalcium aluminate composite pastes under sulfate exposure

Structural Deterioration of Calcium Aluminosilicate Hydrate by Sulfate Attack: Atomic Processes of Al-Si Chain Breaking

Structure, Dynamics and Mechanical Properties Evolution of Calcium Silicate Hydrate Induced by Dehydration and Dehydroxylation

Influences of leaching on the composition, structure and morphology of calcium silicate hydrate (C–S–H) with different Ca/Si ratios

Insight Into the Strengthening Mechanism of the Al-Induced Cross-Linked Calcium Aluminosilicate Hydrate Gel: A Molecular Dynamics Study