Effect of Corrosive Ions (cl − , SO 4 2− , and Mg 2+ ) on the Nanostructure and Chloride Binding Property of C-A-S-H Gel

Shucheng Jin,Kai Liu,Gaozhan Zhang,Hua Shi,Qingjun Ding,Wenyuan Xu

DOI: https://doi.org/10.1007/s11595-020-2356-8

2021-01-01

Journal of Wuhan University of Technology-Mater Sci Ed

Abstract:The nanostructure and chloride binding capacity evolution of C-A-S-H gel exposed to aggressive solutions were investigated, utilizing 29 Si NMR, 27 Al NMR, SEM-EDS, and XRD techniques. The experimental results show that while Cl − ions show a smaller effect on the microstructure of C-A-S-H sample, and SO 4 2− ions can react with C-A-S-H, resulting in decreasing Ca/Si and Al[4]/Si for the C-A-S-H gel ( i e , decalcification and dealuminization). The presence of Mg 2+ ions can aggravate the decalcifying and dealuminizing effects of SO 4 2− ions on the C-A-S-H. With decreasing Ca/Si ratio and aluminum substitution for the original C-A-S-H gel, the depolymerization degree of silicate tetrahedra increases and the calcium aluminosilicate skeleton strengthens. C-A-S-H gel with lower Ca/Si ratio and higher Al[4]/Si ratio shows gentler nanostructure evolution under chemical attack, i e , improving thermodynamic stability under chemical attack. Furthermore, the chloride binding capacity of C-A-S-H gel is decreased after the sulfate attack. Aluminum substitution can also help C-A-S-H gel resist the degraded chloride binding capacity induced by sulfate attack.