Abstract:Using TiO2 nanocrystals (NCs) with diameters of 20 nm (T20), 40 nm (T40) and 60 nm (T60) as starting materials, three TiO2 photo-anodes were constructed on FTO glass. Meanwhile, a triple-layered photo-anode was prepared by depositing the T20, the T40, and the T60 layer by layer on FTO glass (T60/T40/T20/FTO/glass). These four kinds of photo-anodes were sensitized with CdZn0.02S0.08Se0.92 QDs by successive ionic layer adsorption and reaction (SILAR). Based on these photo-anodes, four quantum dot-sensitized solar cells (QDSSCs) were finally obtained. The results indicated that the highest efficiency of 3.95% was obtained in the QDSSC with the triple-layered photo-anode. The short-circuit photocurrent density (J(sc)) of the QDSSC with the triple-layered photo-anode was 1.25, 1.21 and 1.13-fold higher than that of the QDSSCs with T20-, T40- and T60-based photo-anode, respectively. Moreover, with the increase of the average size of the TiO2 NCs from 20 to 60 nm, the Jsc increased from 13.8 to 15.24 mA.cm(-2). The optical properties, crystal structure and morphologies of the bare TiO2 films and the CdZn0.02S0.08Se0.92 sensitized TiO2 photo-anodes were characterized by UV-Vis spectroscopy, XRD and SEM. The incident photon-to-electron conversion efficiency, the open circuit voltage decay and the electrochemical impedance spectroscopy of the QDSSCs were measured and discussed, so as to clarify the underlying mechanism of the property enhancement. (C) 2019 The Electrochemical Society.

Ultralong rutile TiO2 nanorod arrays with large surface area for CdS/CdSe quantum dot-sensitized solar cells

Ultralong Rutile TiO 2 Nanorod Arrays with Large Surface Area for CdS/CdSe Quantum Dot-sensitized Solar Cells

Construction of TiO2 NP@TiO2 NT Double-Layered Structural Photoanode to Enhance Photovoltaic Performance of CdSe/CdS Quantum Dots Sensitized Solar Cells

Synthesis and Characterization of Bi2S3 Quantum Dot-Sensitized TiO2 Nanorod Arrays Coated with ZnSe Passivation Layers

Translucent TiO2 Nanotube Film for Quantum Dots Sensitized Solar Cells

Nanotube Film for Quantum Dots Sensitized Solar Cells

TiO 2 Nanorod Arrays Sensitized with CdS Quantum Dots for Solar Cell Applications: Effects of Rod Geometry on Photoelectrochemical Performance

CdSe/CdS quantum dots co-sensitized TiO 2 nanotube array photoelectrode for highly efficient solar cells

A Novel Method for the Preparation of CdS Quantum Dots Sensitized Solar Cells Based on Free-Standing and Through-Hole TiO2 Nanotube Arrays

CdS/CdSe Co-Sensitized Vertically Aligned Anatase TiO2 Nanowire Arrays for Efficient Solar Cells

Hydrothermal Etching Treatment to Rutile TiO2 Nanorod Arrays for Improving the Efficiency of CdS-Sensitized TiO2 Solar Cells

CdS Quantum Dot-Sensitized Solar Cells Based on Nano-Branched TiO2 Arrays

Cds/Cdse Cosensitized Oriented Single-Crystalline Tio2 Nanowire Array for Solar Cell Application

CdS quantum dots-sensitized TiO2 nanorod array on transparent conductive glass photoelectrodes

A Layered Photo-Anode Prepared Using TiO2 Nanocrystals with Different Sizes for Enhanced Light-Trapping in Quantum Dots-Sensitized Solar Cells

Highly Efficient Quantum Dot-Sensitized TiO2 Solar Cells Based on Multilayered Semiconductors (Znse/cds/cdse).

Toward Highly Efficient CdS/CdSe Quantum Dots-Sensitized Solar Cells Incorporating Ordered Photoanodes on Transparent Conductive Substrates

Quantum-Dots-Sensitized Solar Cells Based on Vertically Ranged Titanium Dioxide Nanotubes

One-step Preparation and Assembly of Aqueous Colloidal CdS(x)Se(1-x) Nanocrystals Within Mesoporous TiO2 Films for Quantum Dot-Sensitized Solar Cells.

Co(SxSe1-x)2 Nanorods Arrays with Rhombus Cross-section Exhibiting High Catalytic Activity for Quantum Dot Sensitized Solar Cells

In situ hydrothermal growth of CdSe(S) nanocrystals on mesoporous TiO 2 films for quantum dot-sensitized solar cells