Abstract:This study aims to investigate a friction stir welded joint between steel and aluminum alloy. FSW is nowadays one of the most interesting joining techniques due to the possibility of connecting materials and thicknesses that are difficult or impossible to weld with traditional techniques. The main advantage is that materials are not affected by thermal cycle problems during solidification and cooling, and the absence of fumes and pollution during the process favors the quality of the welded joint. The life of metal joints could be greatly reduced in a corrosive environment since the less noble material will tend to increase its corrosion rate, while the nobler one will reduce its electrochemical dissolution. Accelerated aging tests (i.e., salt fog test) are used to estimate the lifetime of metal joints in highly aggressive environments. The aim of the present work is to evaluate the durability at a long aging time in the salt spray test (according to ASTM B117) of carbon steel/aluminum alloy joints, obtained by FSW. In this first part, mechanical test results are reported. A deep metallographic and chemical investigation is going to be reported in part two. The current research work investigates the welding direction and residence time in the salt spray chamber. The breakage of all tested samples, evaluated after the tensile tests were carried out, always occurs at the interface of the joint, regardless of the change of direction of the weld on the advancing or retreating side. The welding direction influences the breakage of the joint only before the aging treatment. Specifically, specimens produced in advance are characterized by increased joint strength. On the other hand, the factor that influences the performance of the joints is the exposure time where, starting from the first point of aging, i.e., after two months, there is a decrease in the maximum load of 40%, and the effect of corrosion leads to a significant deterioration of the weld which remains almost similar until the last point of aging.

Fatigue strength of steel–aluminum alloy dissimilar lap joints fabricated by dimple spot welding for automotive application

Dissimilar Al/steel friction stir welding lap joints for automotive applications

Fatigue Behavior of Al/Steel Dissimilar Friction Stir Welds and the Effect of Die‐Press Forming

Dissimilar Friction Stir Lap Welding of Aluminium to Steel: Influence of Alloy Type and Sheet Thickness on Strain Distribution and Failure Location

Depriving friction stir weld defects in dissimilar aluminum lap joints

Mechanical Properties and Failure Behavior of Flow-Drilling Screw-Bonding Joining of Dissimilar Aluminum Alloys under Dynamic Tensile and Fatigue Loading

Fretting Fatigue as a Limiting Factor on the Durability of Friction Stir Welded Lap Joints Using AA2099-T83 and AA2060-T8E30 Aluminium Alloys

Microstructural and interface geometrical influence on the mechanical fatigue property of aluminum/high-strength steel lap joints using resistance element welding for lightweight vehicles: experimental and computational investigation

Experimental Investigation and Characterization of Friction Stir Spot-Welded Dissimilar Aluminum Copper Metallic Lap Joints

Fatigue assessment on 7075/2A12 aluminum alloy friction stir welding lap joints

Experimental Investigation of Material Properties in FSW Dissimilar Aluminum-Steel Lap Joints

Enhancing the mechanical performance of medium-thick Ti/Al dissimilar joints by an innovative double side friction stir Z shape butt-lap welding process

Effect of Loading Methods on the Fatigue Properties of Dissimilar Al/Steel Keyhole-Free FSSW Joints

Evaluation of Corrosion and Its Impact on the Mechanical Performance of Al–Steel Joints

Fatigue Strength Estimation Based on Local Mechanical Properties for Aluminum Alloy FSW Joints

An experimental study on lap joining of multiple sheets of aluminium alloy (AA 5754) using friction stir spot welding

Joining of Dissimilar Al and Mg Metal Alloys by Friction Stir Welding

Fatigue resistance characterization of frictions stir welds between complex aluminum extrusions: An experimental and finite element study

Friction stir riveting (FSR) of AA6061-T6 aluminum alloy and DP600 steel

Microstructure and Mechanical Properties of Mg-Li/Al Dissimilar Joints via Dynamic Support Friction Stir Lap Welding

Durability of Single Lap Friction Stir Welded Joints between S355-J0 Steel and AA5083 Aluminum Alloy–Mechanical Tests