Abstract:Aqueous zinc−iodine battery (AZIB) is a promising energy-storage system due to its high operational safety and the suitable theoretical capacity of 211 mAh g −1 of I 2 . However, it suffers from poor rate performance and low capacity retention due to the easy loss of active substance and the shuttle effect caused by polyiodide species. Herein, we rationally designed a perylene−3, 4, 9, 10−tetracarboxylic anhydride (PTCDA)−based carbon host at the annealing temperature of 900°C (PTCC900) to alleviate the problems mentioned above. PTCC900 embraces a hierarchical porous structure with the pore width ranging from 1.8 nm to 13 nm, which is beneficial for the confinement of I 2 and polyiodide. In addition, the turbostratic graphitic microstructures spread inside PTCC900 also provide fast electronic transmission path to increase the electrical conductivity. Benefitting from the above features, the produced 2 cathode delivers an initial capacity of 240 mAh g −1 and remains a high capacity of 187 mAh g −1 after 600 cycles at the current density of 0.5 A g −1 . More importantly, an ultra−long cycle life of over 50000 cycles is also obtained for 2 when the current density increases to 5 A g −1 . The improved electrochemical performances corroborate that PTCC900 is expected to be a potentially promising cathode host for zinc-iodine batteries.

Hierarchical Porous Soft Carbon Host for the Cathode of an Aqueous Zinc-iodine Battery with Ultra-long Cycle Life