Abstract:The effect of major constituents (the Li content increases from 0.5 to 3 wt% and the Cu content decreases from 4.5 to 2 wt%) on microstructure and mechanical properties of cast Al-Li-Cu-Zr alloy were studied to understand a qualitative assessment of sequence and kinetics of multiple precipitations. Increasing the Li content progressively raises the melting temperature from 520 °C in 1# alloy (Al-0.5Li-4.5Cu, wt%) and 2# alloy (Al-1Li-4.5Cu) to 560 °C in 6# alloy (Al-3Li-2Cu). In addition, the variations of the major constituents result in the changes of the type and volume fraction of the inter- and intra-granular intermetallic phases. TEM results indicate that minor modifications to alloy composition greatly alter precipitation behavior during isothermal aging. The Li-poor alloy (2# alloy) presents a much shorter incubation time of T1-Al2CuLi precipitate than the Li-rich alloy (Al-1.5Li-4.5Cu, 3# alloy), while the nucleation of θ'-Al2Cu precipitate is promoted in Li-rich alloy. No typical spherical δ'-Al3Li precipitate is observed in 2# and 3# alloys during isothermal aging, except for the as-quenched 3# alloy. The preferential nucleation of δ' precipitate on the coherent and broad face of θ' precipitate is observed in 2# and 3# alloys, leading to the formation of "sandwich-like" δ'/θ'/δ' phases. Further decreasing Cu content to 2 wt% and increasing Li content to 3 wt% (6# alloy), the predominant phase in the matrix is δ' precipitate, accompanied by a small amount of unevenly distributed θ' and T1 precipitates. The best balance between ductility and strength is obtained by 2# alloy aged for 32 h, but 6# alloy has significant advantages in terms of density (2.437 g/cm3) and elastic modulus (82.65 GPa) over 2# alloy (density: 2.675 g/cm3; elastic modulus: 75.45 GPa).

Quantitative contribution of T1 phase to the strength of Al-Cu-Li alloys

Theoretical Investigation of Cu Influence on the Stability Characteristics of T-phase in Crossover Alloys

First-principles study of crystal structure and stability of T1 precipitates in Al-Li-Cu alloys

Heterogeneous nucleation of T1 precipitates in solid solution of Al-Cu-Li alloys from Ag-rich structures: An ab initio study

Quantification and Modelling of the Multiphase-Coupled Strengthening Effect in Al-Cu-Li Alloy

Regulation of precipitation behavior among T1, S', and θ' phases in Al–Cu–Li-(Mg–Ag) alloys by optimizing Ag/Mg ratios

Precipitation of T1 Phase in 2198 Al–Li Alloy Studied by Atomic-Resolution HAADF-STEM

Coarsening mechanism of T1 precipitation and calculation of T1/Al interface properties in 2198 Al–Cu–Li alloys: Experimental and DFT studies

Investigation on formation mechanism of T1 precipitate in an Al-Cu-Li alloy

Enhanced matrix precipitation of T1 (Al2CuLi) phase in AA2055 Al–Li alloy during stress aging process

The Nanoscale Strain Assignment Behavior of Icosahedral Quasicrystalline Phase T2-Al6CuLi3 in Cast Al-Li Alloys

Formation mechanism of precipitate T1 in AlCuLi alloys

Combined electron beam imaging and ab initio modeling of T1 precipitates in Al–Li–Cu alloys

Microstructure, tensile properties and fracture behaviour of an Al-Cu-Li-Mg-Zr alloy 8090

Strength-ductility materials by engineering coherent interface at incoherent precipitates

Detailed investigation on microstructure and strengthening contribution of Al- x Cu-1.3Li-X alloy sheets

The effect of major constituents on microstructure and mechanical properties of cast Al-Li-Cu-Zr alloy

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Microstructures and mechanical properties of a cast Al–Cu–Li alloy during heat treatment procedure

Corrosion And Anodizing Behavior Of T-1 (Al2culi) Precipitates In Al-Cu-Li Alloy

Atomic Structure of T1 Precipitates in Al–Li–Cu Alloys Revisited with HAADF-STEM Imaging and Small-Angle X-ray Scattering