Abstract:The initiation and propagation of cracks in polymer electrolyte membranes is not well understood but it is generally considered to be caused by a combination of chemical, mechanical and hygrothermal stressors resulting in combined effects which can accelerate degradation. One such effect is the chemical decomposition of ionomer causing local defects, which can act as crack-initiation sites and can grow under mechanical stresses, leading to enhanced crossover and higher rates of chemical decomposition. It has recently been shown that defect-growth is a good metric to monitor the membrane’s lifetime and fatigue behavior since there exists a correlation between the gas crossover and defect size in membranes. Thus, investigation of crack-growth mechanisms due to mechanical stresses during RH cycling is of great interest for understanding the factors controlling chemical/mechanical durability and developing strategies for improved membrane stability. The mechanical stresses in the membrane are associated with swelling and shrinkage as a result of environmental changes inside the cell during operation. Hydration and heating lead to hygrothermal swelling strains in the membrane. However, the membranes are generally constrained in the fuel cell system by gas diffusion layers (GDL), bipolar plates and gaskets, preventing the membrane from expanding. Consequently, significant compressive stresses can develop. If these stresses exceed the elastic limit, residual tensile stresses may develop during dehydration shrinkage in the membrane. In these cases, the membrane is subjected to cyclical compressive and tensile stresses during the cyclical hydration-dehydration and heating-cooling occurring during fuel cell operation. Such loading is typically referred as fatigue loading and can cause crack propagation. Thus, with the combination of the cyclic fatigue loading and the environmental factors, microcracks can easily initiate and grow into through-thickness cracks, increasing the gas crossover through the membrane and causing the eventual catastrophic failure of the PEM fuel cells. Characterizing this fatigue crack growth under RH cycling is essential for understanding and improving the mechanical durability of PEM fuel cells. Currently, there is very little work on modelling in-situ crack growth in polymer electrolyte membrane and thus far, no attempt has been made to model the in-situ crack-propagation in a membrane using time-dependent viscoelastic-plastic membrane mechanical properties, which is important for an accurate representation of damage accumulation with time. However, considerable research has been devoted to modeling fatigue crack growth in other materials. In 1967, Rice first suggested the use of plastically dissipated energy as a criterion to study fatigue crack propagation in ductile materials. Following the work of Rice, there have been a number of analytical, experimental and numerical investigations into the application of plastically dissipated energy in predicting fatigue crack propagation. In the numerical investigations, the accumulation of plastically dissipated energy under cyclical loading is calculated in a defined region ahead of the crack tip and compared to a critical value, presumed to be a material parameter. Once the accumulation reaches the critical value, the crack propagates via a node release algorithm. In the present work, we develop a numerical simulation to study in-situ crack growth in the through-thickness direction under humidity cycling in a PEM fuel cell model. The temperature-humidity-time-dependent viscoelastic-plastic membrane properties used in the simulation are taken from separate mechanical characterization experiments conducted in our lab. We show that the plastically dissipated energy criterion can qualitatively capture a range of well-established phenomena seen experimentally and in operating fuel cells. Namely; (1) crack propagation in unreinforced perfluorosulfonic acid (PFSA) membrane, (2) crack propagation in expanded polytetrafluoroethylene (ePTFE) reinforced PFSA membrane, (3) the differences between the two, 4) the differences between crack propagation under the channel and land regions in a typical flow channel architecture, (5) the effect of fuel cell clamping pressure on membrane cracking.

Insight into the crack evolution and mechanism of catalyst-coated membrane undergoing freeze–thaw cycling in fuel cells

Influence of crack formation at the catalyst layer and membrane interface on the performance of PEMFC

Investigation of Catalyst Degradation in Proton Exchange Membrane Fuel Cell By Identical Location Electron Microscopy

Effect of Engineered Cracks in Catalyst Layers on PEMFC Catalyst Layer Durability

Investigation of mechanical degradation in catalyst-coated reinforced membranes under in-situ hydrothermal cycles

Effect of Micro-Cracks on the In-Plane Electronic Conductivity of Proton Exchange Membrane Fuel Cell Catalyst Layers Based on Lattice Boltzmann Method

(Invited) Numerical Modeling of the Growth of Fatigue Cracks in PFSA Membranes

A One-Dimensional Numerical Model of Carbon Corrosion in Catalyst Layers of Proton Exchange Membrane Fuel Cells

Nanoscale in-Situ Characterization of Polymer Electrolyte Membrane Fuel Cell Catalyst Layers for Improved Water Management

Effect of catalyst layer on fatigue life and fracture mechanisms of fuel cell membrane

Numerical Evaluation of Crack Growth in Polymer Electrolyte Fuel Cell Membranes Based on Plastically Dissipated Energy

Ratcheting Assessment of the Catalyst Layer in Polymer Electrolyte Membrane Fuel Cells Considering Thermal-Mechanical-humidity Cycling

Ice Formation and Current Distribution in the Catalyst Layer of PEM Fuel Cell at Cold Start

Pore-scale and Multiscale Study of Effects of Pt Degradation on Reactive Transport Processes in Proton Exchange Membrane Fuel Cells

Unraveling the Effects of Carbon Corrosion on Oxygen Transport Resistance in Low Pt Loading Proton Exchange Membrane Fuel Cells

Quantification and evolution on degradation mechanisms of proton exchange membrane fuel cell catalyst layer under dynamic testing conditions

Revealing the Impact of Cell Conditioning on PEMWE Catalyst Layer Morphology

Effects of Cracks on the Mass Transfer of Polymer Electrolyte Membrane Fuel Cell with High Performance Membrane Electrode Assembly

Effect of freeze–thaw cycles on membrane electrode assembly of proton exchange membrane fuel cells and its fault diagnosis method

In-Situ Characterization of Cathode Catalyst Degradation in PEM Fuel Cells

Correlating Catalyst Growth with Liquid Water Distribution in Polymer Electrolyte Fuel Cells