AuPd/Co3O4/3DOM MnCo2O4: Highly active catalysts for methane combustion

Zhuo Han,Lingyun Dai,Yuxi Liu,Jiguang Deng,Lin Jing,Yingxin Zhang,Kunfeng Zhang,Xing Zhang,Zhiquan Hou,Wenbo Pei,Hongxing Dai
DOI: https://doi.org/10.1016/j.cattod.2020.06.068
IF: 5.3
2021-09-01
Catalysis Today
Abstract:Three-dimensionally ordered macroporous (3DOM) MnCo2O4-supported Co3O4 and AuPd (xAuPd z /yCo3O4/3DOM MnCo2O4; x = 0.56–1.98 wt%, z = 1.9–2.1, and y = 4.80–24.36 wt%) catalysts were prepared using polymethyl methacrylate (PMMA) microsphere-templating, incipient wetness impregnation, and polyvinyl alcohol (PVA)-protected reduction methods. Physicochemical properties of the materials were characterized by means of numerous techniques, and their catalytic activities were evaluated for methane combustion. It is found that the xAuPd z /yCo3O4/3DOM MnCo2O4 samples with a surface area of 26.5–53.1 m2/g possessed a high-quality 3DOM architecture, in which the AuPd nanoparticles (NPs) with a size of 4.6–5.8 nm were highly dispersed on the surface of the macropore framework. Among all of the samples, 1.98AuPd2.1/18.20Co3O4/3DOM MnCo2O4 exhibited the highest catalytic activity: the T 10%, T 50%, and T 90% (temperatures required for achieving methane conversions of 10, 50, and 90 %, respectively) were 262, 340, and 408 °C at a space velocity of 40,000 mL/(g h). Partial deactivation of the 1.98AuPd2.1/18.20Co3O4/3DOM MnCo2O4 sample due to introduction of water vapor or carbon dioxide was reversible. It is concluded that the good catalytic performance of 1.98AuPd2.1/18.20Co3O4/3DOM MnCo2O4 was associated with its high adsorbed oxygen species concentration, good low-temperature reducibility, and strong interaction between Co3O4 or AuPd2.1 NPs and 3DOM MnCo2O4.
chemistry, physical,engineering, chemical, applied
What problem does this paper attempt to address?
This paper aims to solve the problems of catalyst activity and stability during the methane combustion process. Specifically, researchers explored the catalytic performance of these materials in methane combustion by preparing catalysts of gold - palladium (AuPd) nanoparticles and cobalt oxide (Co₃O₄) with different loadings on three - dimensionally ordered macroporous manganese - cobalt oxide (3DOM MnCo₂O₄) (denoted as xAuPd_z/yCo₃O₄/3DOM MnCo₂O₄). The main objectives of the study are: 1. **Enhancing catalytic activity**: By introducing AuPd nanoparticles and Co₃O₄, the catalytic activity of the catalyst for methane combustion is enhanced. It was found that the 1.98AuPd₂.₁/18.20Co₃O₄/3DOM MnCo₂O₄ sample exhibited the highest catalytic activity. When the space velocity was 40,000 mL/(g h), the temperatures required for achieving 10%, 50% and 90% methane conversion were 262 °C, 340 °C and 408 °C respectively. 2. **Improving the low - temperature reducibility of the catalyst**: Through X - ray photoelectron spectroscopy (XPS) and hydrogen temperature - programmed reduction (H₂ - TPR) analysis, the oxygen species concentration on the catalyst surface and the low - temperature reducibility were studied. The results showed that the 1.98AuPd₂.₁/18.20Co₃O₄/3DOM MnCo₂O₄ sample had the highest surface - adsorbed oxygen species concentration and good low - temperature reducibility, which helped to improve the catalytic activity. 3. **Evaluating the stability and anti - poisoning ability of the catalyst**: The effects of water vapor and carbon dioxide on the catalyst activity were studied. The results indicated that although water vapor and carbon dioxide could cause partial deactivation of the catalyst, this deactivation was reversible, and after pretreatment, the activity of the catalyst could be restored to the initial level. In summary, through systematically preparing and characterizing catalysts with different compositions, this paper revealed the synergistic effect of AuPd nanoparticles and Co₃O₄ on 3DOM MnCo₂O₄, significantly improved the catalytic performance of methane combustion, and explored the stability and anti - poisoning ability of the catalyst.