Three isostructural Zn/Ni nitro-containing metal-organic frameworks for supercapacitor
Haiyan He,Guojun Wang,Binfeng Shen,Yibin Wang,Zhiyong Lu,Shengping Guo,Jiaxin Zhang,Lu Yang,Quanguo Jiang,Zhenyu Xiao
DOI: https://doi.org/10.1016/j.jssc.2020.121375
IF: 3.3
2020-08-01
Journal of Solid State Chemistry
Abstract:<p>As a novel composite material, metal-organic frameworks have a great application in supercapacitor. In the current study, based on mixed ligands of 5-nitroisophthalic acid (H<sub>2</sub>NIPA) and 1,3-di(4-pyridyl)propane (1,3-dpp), [Zn<sub>3</sub>(NIPA)<sub>3</sub>(1,3-dpp) (H<sub>2</sub>O)<sub>2</sub>·H<sub>2</sub>O]<sub>n</sub> <strong>HU14</strong> and two isostructural [M(NIPA) (1,3-dpp) (H<sub>2</sub>O)·2H<sub>2</sub>O] (M = Zn for <strong>HU15</strong>, M = Ni for <strong>HU16</strong>) were prepared by hydrothermal reaction. The single crystal X-ray diffraction determined that <strong>HU14</strong> contains three different zinc ions to construct a non-porous 3D network, while the isostructure <strong>HU15</strong> and <strong>HU16</strong> display different center metal ions but identical porous frameworks with large brick-like channels. Due to different cations and diverse architectures, these three materials show different electrochemical properties, Ni-MOF(<strong>HU16</strong>) displays a better performance (The specific capacitance of the complexes <strong>HU14</strong>, <strong>HU15</strong> and <strong>HU16</strong> are 22.8 F g<sup>−1</sup>, 27.86 F g<sup>−1</sup> and 307.4 F g<sup>−1</sup> at 1 A g<sup>−1</sup> and remains 60.35%,71.79% and 51% of their capacitance at a high current density of 8 A g<sup>−1</sup>, respectively.) The excellent electrochemical property may be ascribed to the intrinsic nature of Ni-MOF, unique structural feature and the particles of nanoscale size.</p>
chemistry, physical, inorganic & nuclear