MOF-derived binary mixed metal/metal oxide @carbon nanoporous materials and their novel supercapacitive performances

Wang Y. C.,Li W. B.,Zhao L.,Xu B. Q.

DOI: https://doi.org/10.1039/c6cp02374f

IF: 3.3

2016-01-01

Physical Chemistry Chemical Physics

Abstract:Mixed cobalt and manganese oxides embedded in the nanoporous carbon framework (M/MO@C) were synthesized by the direct carbonization of a binary mixed-metal organic framework (CoMn-MOF-74) for the first time. The unique M/MO@C carbon materials maintained the primary morphology of CoMn-MOF-74, and showed a uniform dispersibility of Co, MnO and CoO nanoparticles in the carbon matrix, and therefore greatly increased the conductivity of the M/MO@C materials. A series of M/MO@C samples were tested as the electrode materials for supercapacitors, and a remarkable specific capacitance of 800 F g(-1) was obtained using the M/MO@ C-700 sample at a current density of 1 A g(-1) in 6 M KOH electrolyte. Moreover, the M/MO@C sample showed a good cycling stability with a capacitance retention of 85% after 1000 cycles. It is also found that the optimized carbonization temperature is a critical parameter to obtain such a M/MO@C nanoporous carbon framework with the best capacitive performances. The present approach is convenient and reproducible, which could be easily extended to the preparation of other M/MO@C composites with excellent electrochemical performances.