Abstract:Abstract The porous structure and specific surface area (SSA) of activated carbon (AC) materials are two important factors to determine the performance of supercapacitors, and the emphasis in the current research is on how to regulate the pore structure of AC by an effective method. In this work, the low-cost and widely sourced semi-coke was employed to prepare AC in one step by the chemical activation method, which can effectively decrease the production cost of AC and promotes its application. Orthogonal experiments were designed to reveal the effect of process parameters on the electrochemical performance. It was found that the activator concentration has an important effect on the pore structure. When the mass ratio of the activator to semi-coke (Ras) remained unchanged, the large heating rate would result in a high activator concentration that delivered stronger etching power at the target temperature and thus remarkably affects the pore size and the pore volume of AC. When the heating rate changed from 2 to 7 ℃ min−1, there had a considerable SSA increase of ca. 200 m2 g−1. To further reveal the effect of activator concentration on the pore’s property, the different mass ratios of the activator to semi-coke (Ras) were used. A series of ACs were produced, and the one that was prepared at 600 ℃ in a heating rate of 5 ℃ min−1 in a Ras value of 3:1 delivered a high specific capacitance of 376 F g−1 at 1 A g−1 and a good cycling performance with a capacity retention of 98% after 10,000 cycles at 10 A g−1. This work provided new inspiration for the preparation of high-performance activated carbon with low-cost semi-coke.

A primary understanding of field emission from superhigh specific surface area activated carbon with interconnection structure

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Local Electron Field Emission Study of Two-dimensional Carbon

Enhanced Field-Emission Performance from Carbon Nanotube Emitters on Nickel Foam Cathodes

Field Emission from Dense, Sparse, and Patterned Arrays of Carbon Nanofibers

Field emission from Nanocomposite Carbon

Facile Activation of Commercial Carbon Felt As a Low-Cost Free-Standing Electrode for Flexible Supercapacitors

Synthesis of O-doped coal-based carbon electrode materials by ultrasound-assisted bimetallic activation for application in supercapacitors

Pore-structure Regulation and Heteroatom Doping of Activated Carbon for Supercapacitors with Excellent Rate Performance and Power Density

Field Electron Emission from Carbon Containing Thin Films

Graphitic porous carbon with multiple structural merits for high-performance organic supercapacitor

Synthesis of activated carbon nanospheres with hierarchical porous structure for high volumetric performance supercapacitors

Activated‐carbon‐based supercapacitors with high gravimetric‐ and volumetric capacitance at commercial‐level mass loading

Low Field-Induced Electron Emission Phenomenon Observed from the Carbon Containing Thin Films

Coal-Derived Porous Activated Carbon With Ultrahigh Specific Surface Area And Excellent Electrochemical Performance For Supercapacitors

Field emission from combined structures of carbon nanotubes and carbon nanofibers

Superior integrated field emission cathode with ultralow turn‐on field and high stability based on SiC nanocone arrays

Field emission microscopy of carbon nanotube fibers: evaluating and interpreting spatial emission

Activator concentration regulating the porous structure of activated carbon for supercapacitor application

A high-performance supercapacitor based on activated carbon fibers with an optimized pore structure and oxygen-containing functional groups

A Study on the Field Emission Characteristics of High-Quality Wrinkled Multilayer Graphene Cathodes