Laser pressure welding of copper

Jingquan Zhang,Ting Huang,Sergey Mironov,Dong Wang,Qingwei Zhang,Qiang Wu,Jiejie Xu,Rongshi Xiao

DOI: https://doi.org/10.1016/j.optlastec.2020.106645

2021-02-01

Abstract:<p>Industrial application of copper often requires a joining. Unfortunately, a commercial laser welding of this material is challenging due to extremely high reflectivity of copper at the near-infrared wavelength. In this work, the sound copper joints were produced at relatively high welding speed of 15 m/min by using a pressure-assisted fiber-laser welding. It was theoretically shown that the material melting arisen from a convergence of multiple reflections of the laser beam. By using electron backscatter diffraction (EBSD), it was found that microstructural changes were induced by a laser-induced thermal effect as well as a roller-induced pressure. It was deduced that the molten material solidified before feeding to the pressure rolls and thus it experienced a notable plastic strain during the welding process. The present work provides an effective method for commercial joining of high-reflective metals by using the near-infrared fiber laser.</p>

optics,physics, applied

What problem does this paper attempt to address?

### Problems the paper attempts to solve

This paper attempts to solve the laser welding problems caused by the high reflectivity of copper materials at near - infrared wavelengths. Specifically, because the reflectivity of copper to near - infrared lasers is extremely high (exceeding 95%), it is difficult for traditional laser welding techniques to effectively melt copper materials, and thus high - quality welded joints cannot be achieved. In this paper, this problem is overcome by introducing pressure - assisted fiber laser welding technology, which uses multiple reflections of the laser beam in a V - shaped configuration to concentrate energy.

### Main research contents

1. **Experimental methods**:
- Use commercial T2 copper plates for experiments, with a size of 30 × 1.5 × 1500 mm³.
- Adopt the IPG Photonics Ytterbium Fiber Laser System (YLS - 6000), with a maximum output power of 6 kW and a wavelength of 1.07 μm.
- During the experiment, the welded plates are opened into a V - shaped configuration of 10°, and the laser beam irradiates parallel to the contact point of the two plates.
- During the welding process, the plates move forward under the action of pressure rollers, with a pressure of 400 N.

2. **Theoretical analysis**:
- Through theoretical calculations, the energy concentration phenomenon caused by multiple reflections of the laser beam in a V - shaped configuration is verified.
- The Drude theory is used to describe the transfer process of laser energy to copper materials, and the absorptivity at different incident angles is calculated.

3. **Microstructure analysis**:
- Through electron back - scattering diffraction (EBSD) technology, the microstructure changes in different regions of the welded joint are analyzed.
- The results show that recrystallization occurs in the welding heat - affected zone (HAZ), the grains in the columnar grain zone (CGZ) grow along the direction of the weld centerline, and obvious plastic deformation is observed in the interface region.

### Main conclusions

1. **Successful realization of laser pressure welding of copper**:
- Under the conditions of laser power from 3 kW to 6 kW, welding speed from 5 m/min to 15 m/min, and pressure of 400 N, the laser pressure welding of copper is successfully realized.
- Through theoretical calculations, it is confirmed that multiple reflections in the V - shaped configuration lead to effective concentration of laser energy, increasing the laser power density by about 5 times, thus realizing the melting of materials.

2. **Microstructure changes**:
- Recrystallization occurs in the welding heat - affected zone (HAZ), forming equiaxed grains.
- The grains in the columnar grain zone (CGZ) grow along the direction of the weld centerline, and significant plastic deformation is observed in the interface region, indicating that the material has been partially solidified before rolling.

3. **Application prospects**:
- This research provides an effective method for industrial laser welding of high - reflectivity metal materials, especially of great significance for the application of near - infrared fiber lasers.

Through these studies, the author provides a new idea and technical solution for solving the laser welding problems of high - reflectivity materials.