Recycling of polyester wastes with bio-based alginate fiber into fire-safety composite

Lin Weng,Xiaolin Zhang

DOI: https://doi.org/10.1016/j.polymdegradstab.2023.110519

IF: 5.204

2023-09-01

Polymer Degradation and Stability

Abstract:A depleting fossil reserve and recycling troublesome synthetic fiber waste has become a global crisis when the indecomposable fibers prevails in every aspect of daily life. This work developed a economical and environmentally friendly opening-combing-needle punching technique that recycled polyester waste fibers with intrinsic nonflammable bio-based alginate fibers into a composite up to 50 % of its weight. It had a >26 flame retardancy index and a UL94 V-2 rating, which was in line with cone calorimeter test that had peak of heat release rate of 27.63 kW/m 2 , 38% less than similar alginate fibers/recycled textile fiber composites. Also, the composite generated 27% less smoke in burning than PET fiber felt. Its fire proof mechanism was explored as the dominant charring effect that dense CaCO 3 residue prevented the fiber from burning and exchanging heat/radicals at all stages, which also received support from inert gas dilution of H 2 O evaporated from calcium alginate fiber and easily generated CO 2 , as well as the homogeneous structure of the composite, while the increased CO/CO 2 ratio ruled out the possibility of chemical quenching of active radicals. Taken together, this research recycled synthetic waste fiber into an outstanding fire-proofing composite by a cost-effective and eco-friendly method, which could be a potential filler and construction materials.

polymer science