Abstract:In this study, NiCrSiB-SiC composite coatings were prepared on 16Mn low-carbon steel by vacuum cladding technology using SiC and NiCrSiB mixed powders as raw materials for enhancing their wear resistance. The effects of different content of SiC particles on the microstructure evolution, mechanical and abrasive wear properties of the coatings were investigated. The results showed that SiC particles in all the NiCrSiB-SiC composite coatings with different SiC contents were completely decomposed into C and Si under the catalysis of Ni-based alloy. The out-diffused Si into the coating mainly led to the formation of the Ni 3 Si eutectic phase, while the out-diffused C introduced M 7 C 3 , M 3 C 2 , M 2 (C, B) and other hard phases. Besides, C also diffused to the substrate, leading to a carburizing effect, which remarkably enhanced the mechanical properties of the substrate. In the NiCrSiB-SiC composite coatings with high SiC content, the decomposition of SiC led to the remaining graphite phase. However, once the concentration of SiC was over high, excess graphite would deteriorate the compactness and adhesion of the coating, weakening its wear performance. The nanoindentation and abrasive wear experiments revealed that the composite coating with 5 wt% SiC particles had lower elastic modulus ( E ), higher hardness ( H ), H / E , and H 3 / E 2 , and its wear volume was only 1/10 of that of the substrate, indicating the best mechanical and wear properties. The excellent wear performance can be attributed to the combination of the in-situ formed carbides and borides hard reinforcing phases and the tough coating matrix composed of Fe and Si dissolved γ-Ni and Ni 3 Si eutectic phase.

Microstructure and bond strength of niobium carbide coating on GCr15 prepared by in-situ hot press sintering

Fabrication of Niobium Carbide Coating on Niobium by Interstitial Carburization

Microscopic and macroscopic interfacial studies of NbC reinforcement layer on GCr15 bearing steel surface prepared by in-situ reaction method

Microstructure and Hardness of NbC Coating Produced in Situ

Investigation of the Adhesion Strength and Deformation Behaviour of in Situ Fabricated Nbc Coatings by Scratch Testing

Wear Resistance of In Situ NbC-Reinforced Laser Cladding Ni45 Coatings

Microstructure and Properties of Cr-Nb Carbide Coatings on Graphite Via Powder Immersion Reaction Assisted Coating

Growth and mechanical properties of Nb-Cr carbide coatings on graphite by TRD technique

Refinement of Microstructure and Enhancement of Wear Resistance of Ni–Cr Cast Iron by NbC

Growth Kinetics of In Situ Fabricated Dense NbC Coatings on Gray Cast Iron

Effect of NbC in-situ synthesis on the microstructure and properties of pre-placed WCoB-TiC coating by laser cladding

Structure and Wear Behavior of AlCrSiN-based Coatings

Microstructure evolution, mechanical and abrasive wear properties of NiCrSiB-SiC composite coatings prepared on 16Mn low-carbon steel by Ni-based alloy catalyzed SiC decomposition

Microstructure, Adhesion and Tribological Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrocarburized AISI 4140 Steel

Tailored nanocrystalline Niobium coatings on steel substrates for superior resistance to micro-crack initiation

Machining Performance of Sputter-Deposited (al0.34cr0.22nb0.11si0.11ti0.22)50n50 High-Entropy Nitride Coatings

Effect of in Situ NbC on Microstructure and Wear Properties of Laser Cladding Co-Based Coatings

Microstructure and Wear Resistance of in Situ NbC Particles Reinforced Ni-based Alloy Composite Coating by Laser Cladding

Microstructure and wear properties of niobium carbide particulates gradient-distribution composite layer fabricated in situ

Gradually varying mechanical properties of in situ synthesized NbC–Fe-graded composite coating

Microstructural Evolution and Wear Behaviors of NbC-reinforced Ti-based Composite Coating