LiMnPO4 nanoplates with optimal crystal orientation in situ anchored on the expanded graphite for high-rate and long-life lithium ion batteries

Tu'an Lv,Hao Min,Hongbo Shu,Yujin Zhou,Qianqian Liang,Xiaolong Li,Qiaochu Ren,Zhongyun Ma,Xianyou Wang

DOI: https://doi.org/10.1016/j.electacta.2020.136945

IF: 6.6

2020-11-01

Electrochimica Acta

Abstract:<p>LiMnPO₄ as a positive electrode material for lithium ion batteries has been considered as a potential replacement material for LiFePO₄ because of its 20% higher redox potential than that of LiFePO₄. However, its low electron and lithium ion migration rate make this material an unsatisfactory rate performance and cycle stability. In this work, we report a simple solvothermal route to synthesize a novel "face-to-face" structure for LiMnPO₄/expanded graphene composites, which compose of LiMnPO₄ nanoplatelets with (010) preferential crystal plane in situ grown on expanded graphite. It can be found that the expanded graphite effects on the preferential orientation and morphology of the LiMnPO₄ nanoparticles. In the composites, the "face-to-face" contact structure between the LiMnPO₄ nanoplatelets and expanded graphite sheets provides pathways for rapid electron transfer, meanwhile, the LiMnPO₄ nanoplatelets with (010) preferential crystal plane improve the active sites and shorten the Li ion diffusion distances, resulting in excellent electrochemical performance. It displays an initial discharge capacity of 130 mAhg⁻¹, and capacity retention of 100% after 200 cycles at 1 C. Even at a high rate of 10 C, it still shows a high discharge capacity (102 mAhg⁻¹) and long-life cycle stability (∼72% capacity retention over 1000 cycles).</p>

electrochemistry