Abstract:In this study, a facile strategy is reported for the preparation of porous carbon materials with adjustable pore size through carbonization of MOF-5 at 900 degrees C with the assistance of different additives. Results show that the physical and chemical properties (such as morphology, carbon defect content, BET specific surface area, pore structure) of the porous carbon materials can be adjusted through introduction of different compounds (i.e., C16H32O2, C6H14O6, C18H36O2, Na2CO3, KOH, Cu(NO3)2, NaCl, KCl, MgCl2, ethyl cellulose) during the carbon-ization processes. CO2 adsorption experiment results show that there is a linear relationship between the CO2 adsorption capacity (at 25 degrees C and 0.15 bar) and the cumulative pore volume of pores at 5-7 angstrom, suggesting that pores in the range of 5-7 angstrom play a major role in CO2 adsorption at such condition. While the CO2 adsorption capacity (at 25 degrees C and 0.15 bar) is independent on the BET specific surface area of the materials. Among the prepared porous carbon materials, 5C-C6H14O6-900 exhibits the highest CO2 adsorption capacity (i.e., 3.32 mmol/g at 25 degrees C and 1 bar, 0.88 mmol/g at 25 degrees C and 0.15 bar), with good adsorption/desorption cycle stability and CO2/N2 selectivity. Our work provides a facile and general method to adjust and control the pore size dis-tribution of MOF-derived porous carbon materials. Besides, the analysis results indicate that the micropores in a specific pore size range play a decisive role in the adsorption of CO2 at low pressure, which provides a new idea for the preparation of high-efficiency adsorbents at low pressures.

Reversible Multi‐Complexation of CO2 to Alkaline Earth Metal Ion‐Pair at 400 ppm and 298 K

Combined CO2-philicity and Ordered Mesoporosity for Highly Selective CO2 Capture at High Temperatures

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Anion Pillared Metal–Organic Framework Embedded with Molecular Rotors for Size-Selective Capture of CO2 from CH4 and N2

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

Unravelling the Role of Alkaline Earth Metal Carbonates in Intermediate Temperature CO2 Capture Using Alkali Metal Salt-Promoted MgO-based Sorbents

CO2 capture on micro/mesoporous composites of (zeolite A)/(MCM-41) with Ca2+ located: Computer simulation and experimental studies

Development of Ultramicropore-Mesopore Interconnected Pore Architectures for Boosting Carbon Dioxide Capture at Low Partial Pressure

A Series of Cation-Modified Robust Zirconium-Based Metal-Organic Frameworks for Carbon Dioxide Capture

Controlled Alkali Etching of MOFs with Secondary Building Units for Low-Concentration CO2 Capture.

MOF-derived bimetallic coordination polymer@cobalt-aluminum layered double hydroxide for highly selective CO2 adsorption: Experiments, mechanisms

Cooperative insertion of CO 2 in diamine-appended metal-organic frameworks

Zeolite@Mesoporous silica-supported-amine hybrids for the capture of CO 2 in the presence of water

Synergistic dual-Li+ sites for CO2 separation in metal-organic framework composites

Sustainable Synthesis of Fe-MOR Zeolite for Efficient Capture of CO2

Ultrafast and Stable CO 2 Capture Using Alkali Metal Salt-Promoted MgO-CaCO 3 Sorbents.

Specific K+ Binding Sites As CO2 Traps in a Porous MOF for Enhanced CO2 Selective Sorption

The inorganic cation-tailored “trapdoor” effect of silicoaluminophosphate zeolite for highly selective CO 2 separation

Efficient MgO-based Mesoporous CO2 Trapper and Its Performance at High Temperature.

Reversible and Robust CO2 Capture by Equimolar Task-Specific Ionic Liquid–superbase Mixtures