Abstract:The present work reports the synthesis of a stable aqueous magnetic fluid (AMF) by dispersing double-surfactant-coated Fe3O4 magnetic nanoparticles (MNPs) in water using a facile ambient scalable wet chemical route. MNPs do not disperse well in water, resulting in low stability. This was improved by dispersing double-surfactant (oleic acid and sodium oleate)-coated MNPs in water, where cross-linking between the surfactants improves the stability of the AMFs. The stability was probed by rheological measurements and all the AMF samples showed a good long-term stability and stability against a gradient magnetic field. Further, the microwave spin resonance behavior of AMFs was studied in detail by corroborating the experimental results obtained from the ferromagnetic resonance (FMR) technique to theoretical predictions by appropriate fittings. A broad spectrum was perceived for AMFs which indicates strong ferromagnetic characteristics. The resonance field shifted to higher magnetic field values with the decrease in particle size as larger-size MNPs magnetize and demagnetize more easily since their magnetic spins can align in the field direction more definitely. The FMR spectra was fitted to obtain various spin resonance parameters. The asymmetric shapes of the FMR spectra were observed with a decrease in particle sizes, which indicates an increase in relaxation time. The relaxation time increased with a decrease in particle sizes (sample A to D) from 37.2779 ps to 42.8301 ps. Further, a detailed investigation of the structural, morphological, and dc magnetic properties of the AMF samples was performed. Room temperature dc magnetic measurements confirmed the superparamagnetic (SPM) characteristics of the AMF and the M-H plot for each sample was fitted with a Langevin function to obtain the domain magnetization, permeability, and hydrodynamic diameter of the MNPs. The saturation magnetization and coercivity of the AMF samples increased with the increase in dispersed MNPs’ size of the samples. The improvement in the stability and magnetic characteristics makes AMFs suitable candidates for various biomedical applications such as drug delivery, magnetic fluid hyperthermia, and biomedicines.

Synthesis of Fe3O4/PAM superparamagnetic nano-hydrogels in water-in-oil emulsion

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Preparation of magnetic Fe3O4/PAM composite microspheres by inverse emulsion polymerization

Facile Synthesis, Static, and Dynamic Magnetic Characteristics of Varying Size Double-Surfactant-Coated Mesoscopic Magnetic Nanoparticles Dispersed Stable Aqueous Magnetic Fluids

Synthesis of N-Hexadecylphosphonic Acid-Coated Monodisperse Fe3O4 Superparamagnetic Nanoparticles

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Efficient Oil-Water Separation with Amphipathic Magnetic Nanoparticles of Fe3O4@TiO2

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Preparation of superparamagnetic Fe3O4/PMMA nano composites and their magnetorheological characteristics

Synthesis of Fe<sub>3</sub>O<sub>4</sub> Magnetic Nanoparticles in a Helical Microreactor

Synthesis of Water-soluble Fe3O4 Nanocrystals with a Phase-transfer Method

A Facile Synthesis of Superparamagnetic Hybrid Hollow Nanospheres Based on Monodisperse Nickel–zinc Ferrite/polyethylene Glycol and Their Electromagnetic, Microwave Absorbing Properties

Polydopamine-anchored polyether on Fe3O4 as magnetic recyclable nanoparticle-demulsifiers

A Simple Synthesis of Fe3O4 Nanoclusters and Their Electromagnetic Nanocomposites with Polyaniline

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Study on the magnetic ODSA-in-water Pickering emulsion stabilized by Fe3O4 nanoparticle

Preparation of Monodispersed Hybrid Nanospheres with High Magnetite Content from Uniform Fe3O4 Clusters

Preparation and Characterization of Polydimethylsiloxane Based Magnetic Fluid

Magnetic Nanoparticles with On-Site Azide and Alkyne Functionalized Polymer Coating in a Single Step through a Solvothermal Process

Effect of modified γ-Fe2O3 magnetic nanoparticles on the stability of heavy oil-in-water emulsions

Poly(acrylic acid-co-acrylamide)/Polyacrylamide pIPNs/Magnetite Composite Hydrogels: Synthesis and Characterization