Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Effect of Dendritic Structure and Secondary Phases on the Fatigue Behavior of ERNiCrMo-3 Weld Metal

The Effect of Microstructure on the Fatigue Crack Growth Behavior of Ni-Cr-Mo-V Steel Weld Metal

In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant

Influence of Element Segregation at Grain Boundary of Heat Affected Zone on Low-cycle Fatigue Property of Weldment

The Influence of Heterogeneous Microstructure on Low-Cycle Fatigue Behavior in NiCrMoV Welded Joint

Mechanisms Affecting the Difference in Fatigue Resistance Between Welds and Base Materials Were Investigated Based on In-Situ Fatigue Method

Enhanced Galvanic Corrosion Phenomenon in the Welded Joint of NiCrMoV Steel by Low-Cycle Fatigue Behavior

A Study on Fatigue Crack Propagation for Friction Stir Welded Plate of 7N01 Al-Zn-Mg Alloy by EBSD

Effect of long-term aging on near-threshold fatigue crack growth of Ni–Cr–Mo–V steel welds

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Microstructural Evolution and Liquation Cracking in the Partially Melted Zone of Deposited ERNiCrFe-13 Filler Metal Subjected to TIG Refusion

The Effect of Ferrite Phases on the Micromechanical Response and Crack Initiation in the Intercritical Heat-Affected Zone of a Welded 9cr Martensitic Steel

Very High Cycle Fatigue Behavior And Life Prediction Of A Low Strength Weld Metal At Moderate Temperature

Strain Visualization of Growing Short Fatigue Cracks in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint: Intergranular Cracking and Crack Closure

The Effect of Microstructure and Welding-Induced Plasticity on the Strength of Ni–Mo–Cr Alloy Welds

Investigation on the Fatigue Crack Propagation Behavior of L360MS Pipeline Steel Welded Joints with Inconel 625 Weld Metal

Fatigue crack growth behavior of Ni-Cr-Mo-V steel welded joints considering strength mismatch effect

Very High Cycle Fatigue Behavior of 25cr2ni2mov Steel Welded Joint

The Influence of Prior Austenite Grain Size on Fatigue Crack Growth Threshold of Welds in Cr-Mo-V Steel Components

Effect of Hydrogen Content and Microstructure Inhomogeneity on Fatigue Crack Growth Behavior of Ti-0.3Mo-0.8Ni Alloy Argon-Arc Welded Joints

Effect of Carbon Migration on Interface Fatigue Crack Growth Behavior in 9cr/crmov Dissimilar Welded Joint