Research on energy transfer mechanism and ∼1 μm broadband luminescence properties in Nd3+/Yb3+ co-doped Bi2O3–B2O3–BaF2 glass

Chi Zhang,Kexuan Han,Dechun Zhou,Pengfei Xu,Jilong Cao,Chunlai Song,Chenquan Huang,Sheng Qiang

DOI: https://doi.org/10.1016/j.jlumin.2022.119055

IF: 3.6

2022-09-01

Journal of Luminescence

Abstract:Through the traditional molten method, we designed and fabricated Nd3+/Yb3+ co-doped bismuth borate glasses, and completed the study of the luminescence mechanism of rare earth ions in 1 μm band as well as the doping concentration on the luminescence performance of the glass. Firstly, the thermodynamic properties of the glass sample was evaluated by utilizing DSC curve. Subsequently, the spectral properties of BBFNY-2 glass sample was revealed by analyzing the absorption spectra, fluorescence spectra, fluorescence lifetimes and Judd-Ofelt (J-O) theory. Finally, the energy transfer mechanism between rare earth ions Nd3+→Yb3+ was analyzed in detail. The increase of fluorescence intensity at 1008 nm in the glass was calculated corresponding to the broadening of Δλeff from 103 nm to 107 nm, and the obtainable OCT (optical coherence tomography) axial resolution increased from 4.4 μm to 4.1 μm. In this work, the small absorption cross section of Yb3+ at 980 nm in 55Bi2O3–35B2O3–10BaF2 (mol%) glass is effectively solved by Nd3+→Yb3+ energy transfer. Meanwhile, the relevant parameters of the prepared BBFNY-2 glass sample were calculated, and the results suggested that the fabricated glass samples have large microscopic parameters, high transfer efficiency and long fluorescence lifetime. In the results, it was revealed that the via non-radiative electric dipole-dipole process was responsible for the energy transfer and was proportional to the concentration of the Nd3+ donor ions. With all the results, the prepared BBFNY-2 glass sample is a high-potential candidate material for ∼1 μm laser applications.

optics