NIR luminescence from Er–Yb, Bi–Yb and Bi–Nd codoped germanate glasses for optical amplification

G. Lakshminarayana,Jian Ruan,Jianrong Qiu

DOI: https://doi.org/10.1016/j.jallcom.2008.09.135

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:In this paper, we present the near-infrared luminescence from Er-Yb, Bi-Yb, Bi-Nd codoped germanate glasses. Compared with Bi-doped glass, Bi-Yb codoped glass has shown broad infrared luminescence under 800 nm excitation wavelength. The near-infrared spectra of Er3+-Yb3+ and Bi and Bi-Yb codoped glasses have shown full width at half maximum (FWHM) around 80 nm, 240 nm and 300 nm, respectively, under 980 nm and 800 turn LD. The absorption band of the Yb3+ ion was located around 980 nm. Though the absorption band of Yb3+ does not interact directly with the incident light at 800 nm, near-infrared emission intensity has been highly increased in Bi-Yb codoped glass. We explained the relevant mechanism for the observed enhancement in the near-infrared emission intensity of Bi doped glass with Yb codoping under 800 nm excitation. The measured lifetimes of Bi, Bi-Yb codoped glasses were 490 mu s and 815 mu s, respectively. The maximum stimulated emission cross sections for 1188 nm and 1258 nm emission bands of Bi and Bi-Yb codoped glasses were 9.003 x 10(-21) cm(2) and 5.445 x 10(-21) cm(2). These Er3+-Yb3+, Bi-Yb and Bi-Nd codoped glasses are promising materials for broadly tunable laser sources and broadband optical amplifiers. (C) 2008 Elsevier B.V. All rights reserved.