Abstract:Abstract. In the present paper, carbon nanotubes (CNTs) were synthesized by arc discharge method by vaporizing graphite rods in the presence of Ni and a Ni/Y mixture as catalysts for subsequent use in electrical energy storage and conversion devices. CNTs synthesis was carried out in a cylindrical glass reactor applying a controlled Argon flow of 1.43 cm3/min and a chamber pressure of 39 kPa. Carbon powder was collected from the reactor following chemical treatment with HCl solution at 1 M to remove the metallic impurities. Morphology obtained by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) showed multi-walled nanotubes (MWCNTs) with amorphous carbon particles attached to their surface. Fourier transform infrared (FT-IR) spectra presented bands at 1550 and 1200 cm–1 corresponding to the C=C bond characteristic to the CNTs skeleton; these bands were not present in pristine graphite. Electromagnetic absorbance was observed using ultraviolet-visible spectroscopy (UV-Vis) showing peaks at 204 and 256 nm related to sp2 hybridization characteristic for MWCNTs. Resumen. En el presente trabajo se sintetizaron nanotubos de carbono (NTCs) por el método de descarga de arco mediante la vaporización de barras de grafito en presencia de Ni y una mezcla de Ni/Y como catalizadores para su posterior uso en dispositivos de almacenamiento y conversión de energía eléctrica. La síntesis de NTCs se realizó en un reactor cilíndrico de vidrio aplicando un flujo controlado de Argón de 1.43 cm3/min y una presión de cámara de 39 kPa. El polvo de carbón se recolectó del reactor y se trató químicamente con una solución de HCl a 1 M para eliminar las impurezas metálicas. La morfología obtenida por microscopía electrónica de barrido (MEB) y microscopía electrónica de transmisión (MET) mostró nanotubos de paredes múltiples (NTCPMs) con partículas de carbón amorfo adheridas a su superficie. Los espectros de infrarrojo transformada de Fourier (FT-IR) mostraron bandas en 1550 y 1200 cm–1 que corresponden al enlace C=C característico de los NTCs; estas bandas no estuvieron presentes en el grafito prístino. La absorbancia electromagnética se observó mediante espectroscopia ultravioleta-visible (UV-Vis) mostrando picos a 204 y 256 nm relacionadas con la hibridación sp2 característica de los NTCPMs.

Green synthesis and characterization of multiwall carbon nanotubes from sugarcane bagasse as a biogenic catalyst via chemical vapour deposition method using LPG as hydrocarbon source

Pyrolyzing Renewable Sugar and Taurine on the Surface of Multi-Walled Carbon Nanotubes As Heterogeneous Catalysts for Hydroxymethylfurfural Production

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Synthesis of multi-walled carbon nanotubes by thermal CVD technique on Pt–W–MgO catalyst

Study of Multi-Walled Carbon Nanotube Structures Fabricated by PMMA Suspended Dispersion

Growth and Characterization of Multi-Walled Carbon Nanotubes using Chemical Vapor Deposition

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Efficient eco-friendly synthesis of carbon nanotubes over graphite nanosheets from yellow corn: a one-step green approach

SYNTHESIS OF SINGLE-WALLED CARBON NANOTUBES FROM LIQUEFIED PETROLEUM GAS

Catalytic Chemical Vapor Deposition Methodology for Carbon Nanotubes Synthesis

Carbon nanotubes synthesis over coal ash based catalysts using polypropylene waste via CVD process: Influence of catalyst and reaction temperature

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Purification of Multi Walled Carbon Nanotubes (Mwcnts) Synthesized by Arc Discharge Set Up

Evaluating the characteristics of multiwall carbon nanotubes

Pyrrolic nitrogen-doped multiwall carbon nanotubes using ball-milled slag-SiC mixtures as a catalyst by aerosol assisted chemical vapor deposition

Synthesis of Carbon Nanotubes via Liquid Injection Chemical Vapour Deposition as a Vector for the Chemical Recycling of Waste Composite Carbon Sources

Controllable Synthesis of CNTs Using Pd Catalyst

Synthesis of multi-walled carbon nanotubes on nichrome and nickel by using rapid thermal processing furnace

Synthesis and characterization of hierarchical suspended carbon fiber structures decorated with carbon nanotubes

Synthesis of carbon nanotubes by arc-discharge and chemical vapor deposition method with analysis of its morphology, dispersion and functionalization characteristics

Multi-walled Carbon Nanotubes Synthesis by Arc Discharge Method in a Glass Chamber