Pengfei Li,Yingbo Chen,Fan Xiao,Ming Cao,Jingyu Pan,Jingfeng Zheng,Hao Li,Ke Zhao,Xianglin Zhang,Yuanyuan Zhang
DOI: https://doi.org/10.1007/s10853-023-08903-8
IF: 4.5
2023-09-09
Journal of Materials Science
Abstract:An efficient strategy for increasing the proton conductivity of proton exchange membranes (PEMs) is the introduction of functionalized metal–organic frameworks (MOFs) to establish efficiency proton conduction channels. In this work, a sub-structure fragment flexible bifunctional MOFs UiO-66-NH-SO 3 H was successfully prepared. Next, UiO-66-NH-SO 3 H was filled with sulfonated poly (ether ether ketone) (SPEEK) to prepare composite PEMs. The sub-structure fragment of the UiO-66-NH-SO 3 H functioning as both a donor and an acceptor can promote rapid proton conduction. Furthermore, an effective channel for proton conductivity might be constructed by creating acid–base pairing interaction between the –NH/–NH 2 on the UiO-66-NH-SO 3 H sub-structure fragment and the –SO 3 H on the backbone of SPEEK. At 80 °C and 100% relative humidity (RH), the UiO-66-NH-SO 3 H/SPEEK = 30% composite PEMs has the maximum proton conductivity of 0.273 S cm −1 , which is 84% higher than the SPEEK membrane. Finally, because of the remarkable compatibility between UiO-66-NH-SO 3 H and SPEEK, the UiO-66-NH-SO 3 H/SPEEK = 40% composite PEMs had the maximum proton conductivity of 0.232 S cm −1 , the lowest methanol permeability of 4.67 × 10 –7 cm 2 s −1 and the highest proton selectivity of 21.79 × 10 4 S s cm −3 . This work offers a design and construction method for MOFs with precise structural functionalization to enhance proton conductivity and prevent methanol permeability in PEMs. Thus, the prepared composite PEMs is promising for DMFCs applications.
materials science, multidisciplinary