Abstract:Fabric-based supercapacitor electrodes were fabricated by embedding spread tow carbon fiber fabrics, in monolithic, bicontinuous carbon aerogels (CAG). The incorporation of CAG, at less than 30 wt%, increased the specific surface area of the CAG-CF fabric to above 230 m2 g−1 and the pore volume to about 0.35 cm3 g−1, orders of magnitude higher than that for the as-received carbon fibres. The presence of the CAG not only improves the electrochemical performance of the composite electrodes but may enhance the mechanical response due to the high stiffness of the aerogel structure. Cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance measurements were performed on symmetric supercapacitor cells consisting of two CAG-reinforced fabrics in an ionic liquid electrolyte. The specific capacitance of the symmetric supercapacitor was determined to be in the range 3–5 F g−1, considerably higher than that for the plain carbon fibers. Since optimum structural electrolytes are not yet available, this value was normalized to the total mass of both electrodes to place an upper bound on future structural supercapacitors using this spread tow CAG-CF system. The maximum specific energy and specific power, normalized to the total mass of the electrodes, were around 2.64 W h kg−1 and 0.44 kW kg−1, respectively. These performance metrics demonstrate that the thin CAG-modified spread tow fabrics are promising electrodes for future use in structural supercapacitors. In principle, in future devices, the reduced ply thickness offers both improved mechanical properties and shorter ion diffusion distance, as well as opportunities to fabricate higher voltage multicell assemblies within a given component geometry.

Surface activated commercial carbon cloth as superior electrodes for symmetric supercapacitors

Monocrystalline FeMnO3 on Carbon Cloth for Extremely High-Areal-Capacitance Supercapacitors

Facile Activation of Commercial Carbon Felt As a Low-Cost Free-Standing Electrode for Flexible Supercapacitors

Simple Air Calcination Affords Commercial Carbon Cloth with High Areal Specific Capacitance for Symmetrical Supercapacitors

Boosting Supercapacitive Performance of Flexible Carbon Via Surface Engineering.

Hydrothermal activated carbon cloth as electrode materials for symmetric supercapacitors

Surface functional treatment of carbon fiber with ultra wide potential range in neutral electrolyte for high performance supercapacitor

A novel two-prong strategy to boost the capacitive performance of commercial carbon cloth

Electrochemical performance of supercapacitor electrodes based on carbon aerogel-reinforced spread tow carbon fiber fabrics

Surface Modifications of Carbon Fiber Electrodes for Structural Supercapacitors

Wearable High‐Performance Supercapacitors Based on Silver‐Sputtered Textiles with FeCo2S4–NiCo2S4 Composite Nanotube‐Built Multitripod Architectures As Advanced Flexible Electrodes

Flexible carbon cloth supercapacitors with high power and energy densities

Enhancing the Capacity of Activated Carbon Electrodes by a Redox Mediator Pair for the Fabrication of Flexible Asymmetric Solid-State Supercapacitors

Structural and surface engineering promotes Zn-ion energy storage capability of commercial carbon cloth

Carbon fabric supported 3D cobalt oxides/hydroxide nanosheet network as cathode for flexible all-solid-state asymmetric supercapacitor

Cotton fabrics-derived flexible nitrogen-doped activated carbon cloth for high-performance supercapacitors in organic electrolyte

Kenaf-based activated carbon: A sustainable solution for high-performance aqueous symmetric supercapacitors

High-Performance Supercapacitors Based on Graphene/Activated Carbon Hybrid Electrodes Prepared Via Dry Processing

Carbon cloth as an advanced electrode material for supercapacitors: progress and challenges

MXene-coated Silk-Derived Carbon Cloth Toward Flexible Electrode for Supercapacitor Application

High-performance Compressible Supercapacitors Based on Functionally Synergic Multiscale Carbon Composite Textiles