Abstract:The morphology and mechanical properties of PVA were studied using atactic poly(vinyl alcohol) (at-PVA) dry gel films prepared by crystallization from solutions in dimethyl sulfoxide (Me2SO) and water (H2O) mixtures, in which Me2SO/H2O composition was set to be 60:40. The hot homogenized solution was quenched by pouring it into an aluminum tray controlled at −80°C, thus generating a gel. The crystal lattice modulus along the chain axis was measured by X-ray diffraction. The values were 200–220GPa, which is independent of temperature up to 170°C. However, the values became lower with further increase in temperature and the value at 200°C became 133GPa. This tendency is different from the previous reports showing rapid decrease in the crystal modulus at higher temperature than 120°C. The difference means that crystallites within the specimens prepared by quenching the solution (Me2SO/H2O=60:40) at −80°C are in much more stable state than those of the previous specimens. In spite of the temperature independence of the crystal modulus along the chain axis and the crystallinity, the storage modulus similar to Young's modulus decreases gradually with increasing temperature. To study the mechanical properties and molecular orientation of the present specimens with the stable crystallites, the orientational behavior of crystallites was estimated in terms of the orientation distribution function of crystallites, and Young's modulus was calculated by using the generalized orientation factors of crystallites and amorphous chain segments estimated from the orientation functions of crystallites and amorphous chain segments. In doing so, the theoretical calculation was carried out by using a three-dimensional model, in which the oriented crystalline layers are surrounded by an anisotropic amorphous phase and the strains of the two phases at the boundary are identical. The theoretical values were in good agreement with the experimental ones. The 13C NMR measurements suggested that the inter-molecular hydrogen bonds may be broken by drawing and the intra-molecular hydrogen bonds are more preferably formed in the mm and mr sequences with draw ratio but no marked difference in the structure exists between the crystalline and non-crystalline regions, as judged from the hydrogen bonding in the triad sequences. Even so, the spin–lattice relaxation time, T1C, decreased drastically with increasing temperature reflecting drastic activity of chain mobility. Accordingly, the drastic decrease in Young's modulus (the storage modulus) is thought to be due to the fact that chain mobility in the amorphous phase becomes more pronounced as temperature increases.

Change in the Morphology and Properties of Poly(vinyl alcohol) Cryogels Depending on the Annealing Temperature

Effects of Crystallization Temperature of Poly(vinylidene Fluoride) on Crystal Modification and Phase Transition of Poly(butylene Adipate) in Their Blends: a Novel Approach for Polymorphic Control.

Preparation of Poly(ethylene Glycol) Aligned Porous Cryogels Using a Unidirectional Freezing Technique

Study of Cryostructuring of Polymer System. 65. Features of Changes in the Physicochemical Properties of Poly(vinyl alcohol) Cryogels Caused by the Action of Aqueous Solutions of Amino Acids of General Formula H2N–(CH2)n–COOH

Study of Cryostructuring of Polymer System. 66. Properties and Microstructure of Poly(vinyl alcohol) Cryogels Formed in Frozen Dimethyl Sulfoxide with Additives of Urea and Then Hydrated by Replacing Organic Medium with Water

Cryostructuring of Polymeric Systems: 67 Properties and Microstructure of Poly(Vinyl Alcohol) Cryogels Formed in the Presence of Phenol or Bis-Phenols Introduced into the Aqueous Polymeric Solutions Prior to Their Freeze–Thaw Processing

Effect of initial freezing temperature and comonomer concentration on the properties of poly(aniline-co-m-phenylenediamine) cryogels supported by poly(vinyl alcohol)

Effect of Polyfluorinated Alcohols on Properties of Polyvinyl Alcohol Cryogels

Behaviors of Water Molecules in Polyvinyl Alcohol Gel Amid Stretch and Temperature Changes: A Molecular Dynamics Study

Investigations of morphological changes during annealing of polyethylene single crystals

Structure and Morphology of Freeze/Thawed PVA Hydrogels

Research on the Thermal Aging Mechanism of Polyvinyl Alcohol Hydrogel

Influence of annealing treatment on the structure and properties of poly(4-methyl-1-pentene)-based films and membranes

Insight into the Annealing Peak and Microstructural Changes of Poly(L-Lactic Acid) by Annealing at Elevated Temperatures

Effect of Annealing on Microstructure and Mechanical Properties of Polypropylene Random Copolymer

Thermal Behavior of Poly(vinyl alcohol) in the Form of Physically Crosslinked Film

Thermally Tunable Dynamic and Static Elastic Properties of Hydrogel Due to Volumetric Phase Transition

Effects Of Thermal-Treatment On Poly(Ether Ether Ketone)

Temperature Dependence of the Morphology and Mechanical Properties of Poly(vinyl Alcohol) Drawn Films Prepared by Gelation/crystallization from Solutions by X-ray and Solid State 13C NMR

Effects of Chemical Cross-Linking and Heat Treatment on Polyvinyl Alcohol Membrane Performance

Effects of Annealing on the Hierarchical Crystalline Structures and Mechanical Properties of Injection‐molded Bars of High‐density Polyethylene