Anomalous martensitic transformation with diffusion in the all- d -metal Heusler alloys of Ni 2 MnTi and Ni 2 MnV from first-principles investigation

Chun-Mei Li,Bo Jiang,Yu-Tong Liu,Ren-Zhong Huang
DOI: https://doi.org/10.1016/j.rinp.2024.107397
IF: 4.565
2024-01-29
Results in Physics
Abstract:Using the first-principles exact muffin-tin orbitals method in combination with the coherent potential approximation, the Ti- and V-alloying effects on the crystal structure and lattice parameter, phase stability, magnetic and elastic properties of Ni 2 MnGa have been systematically investigated with Ni 2 MnGa 1−x Z x′ (Z ′x , Z ′ =Ti and V, 0≤x≤1 ) Heusler alloys. It is shown that the two all- d -metal alloys of Ni 2 MnZ ′ are both stabilized by the simple-tetragonal (ST) structure with c/a being very close to 1. The Ti- and especially V-doping can increase both the tetragonal lattice deformation ( |1−c/a| ) of the body-centered-tetragonal (BCT) martensite and the energy barrier between the phase and the parent L21 one, and then favor improving the martensitic transformation (MT) in Ni 2 MnGa. However, since the relative energy of the ST structure decreases more rapidly with increasing x , these Ti x ( x>0.3 ) and V x ( x>0.2 ) alloys are supposed to occur an anomalous MT with diffusion instead, L21 -BCT-ST, where the ST structure is transformed only by Mn and Ga/Z ′ atoms on their second layer of the BCT one swapping the positions, because of c/a of the latter phase being right almost 2 c/a of the former one. The strong anti-ferromagnetic coupling between Mn and Z ′ atoms is further proved to be responsible for energetically promoting the anomalous MT with Z ′ -doping. During these phase transitions, the shear elastic constant C′=(C11−C12)/2 of Ni 2 MnV softens to be negative more easily, and then the Ti-doping is more beneficial to enhance the ductility of Ni 2 MnGa. The anomalous MT is finally confirmed also originating from the Jahn–Teller instability, dominated by 3 d electrons of Ni and Ti in the Ti x but Ni, Mn, and V in the V x alloys.
physics, multidisciplinary,materials science
What problem does this paper attempt to address?