Abstract:The thermal stability of the dual phase AlCrFeCoNiCu 0.5 high entropy alloy thin films at up to 600 °C under vacuum was studied through detailed characterization. The evolution of microstructure and chemical composition was revealed by X-ray diffraction, transmission Kikuchi diffraction and transmission electron microscopy . Also, the mechanical properties were measured by nanoindentation . Although the crystalline phase of all the HEA thin films was BCC-dominated, the FCC phase fraction increased from 16.6% (as-deposited) to 28.1% (600 °C-annealed). The as-deposited films exhibited a columnar morphology with an average grain size of 106.1 nm for length and 31.3 nm for width and remained the columnar shape until 600 °C. The columnar grains showed an increasing tendency of size at 200 °C (221.3 nm and 45.6 nm for length and width) and 400 °C (283.9 nm and 56.2 nm). At 600 °C, the columnar grain size decreased to 211.8 nm in length and 59.3 nm in width. Concurrently, the occurrence of new equiaxed grains was observed with an average diameter of 42.4 nm. The reduction of columnar grain size and the formation of equiaxed grains at 600 °C were explained based on the energy dispersive spectroscopy. Although no preferential evaporation was found, the elemental distribution revealed the formation of two secondary phases, i.e., Cu-rich FCC phase and Cr-rich BCC phase. The nanoindentation results indicated that the mechanical properties increased as the increase of annealing temperature. The hardness and elastic modulus of 600 °C-annealed sample were 8.5 ± 0.3 GPa and 205.4 ± 3.5 GPa, respectively, which were 10.4% and 41.5% higher than those of the as-deposited thin film. These findings are critical for a fundamental understanding of the microstructure and properties change of the dual-phase HEA thin films in high working temperatures.

Extreme thermal stability in crystal-amorphous nanocrystalline CoCrFeMnNi high entropy alloy

Ultrahigh Cryogenic Strength and Exceptional Ductility in Ultrafine-Grained CoCrFeMnNi High-Entropy Alloy with Fully Recrystallized Structure

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Nanostructured Oxide‐Dispersion‐Strengthened CoCrFeMnNi High‐Entropy Alloys with High Thermal Stability

Exceptional Thermal Stability of Additively Manufactured CoCrFeMnNi High-Entropy Alloy with Cellular Dislocation Structures

Excellent thermal stability and mechanical properties of bulk nanostructured FeCoNiCu high entropy alloy

Microstructure evolution and mechanical behavior of a CoCrFeNiMn0.75Cu0.25 high-entropy alloy by thermo-mechanical treatment

Introducing a new heterogeneous nanocomposite thin film with superior mechanical properties and thermal stability

Effect of Co on phase stability and mechanical behavior of CoxCrFeNiMnAl0.3 high entropy alloys with micro/nano hierarchical structure

Ultra-small-angle neutron scattering study on temperature-dependent precipitate evolution in CoCrFeNiMo0.3 high entropy alloy

Accelerated Discovery of (TiZrHf)x(NbTa)1‐x High‐Entropy Alloys with Superior Thermal Stability and a New Crystallization Mechanism

Precipitation and decomposition in CoCrFeMnNi high entropy alloy at intermediate temperatures under creep conditions

Effect of Annealing Temperature on the Microstructure and Mechanical Properties of CoCrFeNiNb0.2Mo0.2 High Entropy Alloy

Ultrahigh hardness with exceptional thermal stability of a nanocrystalline CoCrFeNiMn high-entropy alloy prepared by inert gas condensation

The microstructural evolution of dual phase high entropy alloy thin films by annealing

Thermal stability of electrodeposited nanostructured high-entropy alloys

Rapid amorphization of CrMnFeCoNi high-entropy alloy under ultrasonic vibrations

Structural evolution during mechanical milling and subsequent annealing of Cu–Ni–Al–Co–Cr–Fe–Ti alloys

Microstructure of and mechanical properties of an as-cast fine-grain dual-phase Fe-based high entropy alloy formed via solid-state phase transformation

Nanocrystalline High-Entropy Alloys: A New Paradigm in High-Temperature Strength and Stability

The phase stability at intermediate-temperature and mechanical behavior of the dual-phase AlCoCr0.5FexNi2.5 high entropy alloys