Abstract:The application of organic coatings is the most cost-effective and common method for metallic equipment toward corrosion, whose anti-corrosion property needs to be improved and evaluated in a short time. To rapidly and rationally assess the anti-corrosion property of organic coatings in the ocean splash zone, a new accelerated test was proposed. In the study, the corrosion protection property of the coating samples was measured by an improved AC-DC-AC test in a simulated seawater of 3.5 wt.% NaCl solution, a simulated ocean splash zone test and a new accelerated test combining the above two tests. The results showed that the corrosion rate of the coating samples was high in the improved AC-DC-AC test, which lost its anti-corrosion property after 24 cycles equal to 96 h. The main rapid failure reason was that the time of the water and corrosive media arriving at the carbon steel substrate under the alternating cathodic and anodic polarization with symmetrical positive and negative electric charges was shortened. The entire impedance of the coating samples was improved by about 1.6 times more than that in the initial early time in the simulated ocean splash zone test, which was caused by the damage effect from the salt spraying, drying, humidifying, salt immersion, high temperature and UVA irradiation being weaker than the enhancement effect from the post-curing process by the UVA irradiation. In the new accelerated test, the samples lost their corrosion resistance after 12 cycles equal to 288 h with the fastest failure rate. On account of the coupling process of the salt spraying, drying, humidifying, salt immersion, high temperature combined with the cathodic and anodic polarization and the UVA irradiation, the penetration and transmission rate of water and corrosive media in the coating were further accelerated, the corrosion rate on the carbon steel substrate was reinforced even larger and the destruction of the top polymer molecules was more serious. The new accelerated test showed the strongest damage-acceleration effect than that in the other two tests.

Assessment of Anti-Corrosion Performances of Coating Systems for Corrosion Prevention of Offshore Wind Power Steel Structures

The corrosion protection performance of repair coatings for offshore wind power constructions after long‐term splash zone site exposure

Evaluation of Anticorrosion Coatings for Offshore Wind Turbine Monopiles for an Optimized and Time-Efficient Coating Application

The performance of a self‐adherent foil system for the corrosion protection of steel substrates for offshore wind tower structures

Corrosion Protection Systems and Fatigue Corrosion in Offshore Wind Structures: Current Status and Future Perspectives

Metallic coatings in offshore wind sector—a mini review

Anti-corrosion Control in the Offshore Steel Structure

Recent advances on organic coating system technologies for corrosion protection of offshore metallic structures

Investigating Corrosive Environmental Factors and Corrosion Rate to Assess Vulnerable Corrosive Areas of Offshore Bridges

Effect of Surface Roughness on Corrosion Resistance of Mooring Chains for Offshore Floating Photovoltaics

Corrosion threshold data of metallic materials in various operating environment of offshore wind turbine parts (tower, foundation, and nacelle/gearbox)

Review of corrosion monitoring and prognostics in offshore wind turbine structures: Current status and feasible approaches

Quality control for anticorrosion and coating at offshore platform dock

Design of ICCP Cathodic Protection System for Offshore Wind Power Jacket

Polarization-Accelerated Seawater Splash Simulation for Rapid Evaluation of Protection Performance of an Epoxy Coating on Carbon Steel

Artificial Weathering Test Methods of Waterborne Acrylic Coatings for Steel Structure Corrosion Protection

On the Durability Performance of Two Adhesives to Be Used in Bonded Secondary Structures for Offshore Wind Installations

Corrosion issues and monitoring techniques for offshore wind turbine foundations

Experimental study on interfacial bond-slip behavior of weathering steel and seawater sea-sand concrete in corrosive marine environments

Anticorrosion behavior of organic offshore coating systems in UV, salt spray and low temperature alternation simulated Arctic offshore environment

Corrosion behaviour of welded low-carbon steel in the Arctic marine environment