Assessment of Thermal Aging and Moisture Content in Medium Voltage XLPE Cable from Polarization Current Measurements

Aadil Jamshed,Nasirul Haque

DOI: https://doi.org/10.1109/tdei.2024.3352534

IF: 2.509

2024-01-01

IEEE Transactions on Dielectrics and Electrical Insulation

Abstract:In this work, a methodology has been presented to assess the thermal aging condition and moisture content of XLPE cable insulation from a single polarization current measurement. For this purpose, polarization current measurements were performed on several specimens of 11kV XLPE having varied degrees of moisture content and thermal aging. The moisture content was introduced in the aged and unaged specimens through very small artificial holes of 0.5mm diameter. From the polarization current measurements, various features were extracted using a five-parameter power law-based dielectric response modelling and a modified version of isothermal relaxation current analysis. Following this, an efficient feature selection algorithm analysis of variance (ANOVA) was used to select the best features prior to classification based on thermal aging using three well-known machine classifiers (ML), namely, cubic support vector machine (SVM), extreme gradient boost (XGBoost) and random forest algorithm (RFA). All samples, irrespective of the moisture content, were classified into five classes with an accuracy of 99.5%, 97.5%, and 98%, respectively. After that, a moisture-sensitive parameter is identified that is capable of predicting the moisture content quantitatively in each of the aging classes with satisfactory.

engineering, electrical & electronic,physics, applied