Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Magnetic Chains Created by Polymer-Induced Assembly of Hollow Cobalt Nanoparticles

Chain-Like Structure Created by Assembly of Cobalt Nanoparticles Using Pvp As Soft Template

Nickel Chains Assembled by Hollow Microspheres and Their Magnetic Properties

Uniform Magnetic Chains of Hollow Cobalt Mesospheres from One-Pot Synthesis and Their Assembly in Solution

Synthesis and Magnetic Properties of Chain-like Cobalt Assemblies

Dipolar Chains and 2D Aligned Stripes of Polymer‐coated Magnetic Iron Colloid

Simple Electroless Synthesis of Cobalt Nanoparticle Chains, Oriented by Externally Applied Magnetic Fields

Magnetic nanochains of metal formed by assembly of small nanoparticles.

CTAB-mediated synthesis of iron–nickel alloy nanochains and their magnetic properties

Template-Free Synthesis of Magnetic Chains Self-Assembled from Urchin-Like Hierarchical Ni Nanostructures

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Chain Assembly Kinetics from Magnetic Colloidal Spheres

Ferromagnetism: Self‐Assembled Platinum Nanochain Networks Driven by Induced Magnetic Dipoles (adv. Funct. Mater. 7/2014)

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Cobalt–iron cyanide hollow cubes: Three-dimensional self-assembly and magnetic properties

Necklace‐like Noble‐Metal Hollow Nanoparticle Chains: Synthesis and Tunable Optical Properties

Self‐Assembled Platinum Nanochain Networks Driven by Induced Magnetic Dipoles

Shear disassembly of hierarchical superparamagnetic Fe3O4 hollow nanoparticle necklace chains

Microstructure and Local Magnetic Induction of Segmented and Alloyed Pd/Co Nanocomposites Encapsulated Inside Vertically Aligned Multiwalled Carbon Nanotubes

Single-Chain Janus Nanoparticle by Metallic Complexation

Hydrothermal Synthesis and Magnetic Properties of Co-Ni Alloy Chains