Preparation of Polyvinyl Alcohol (PVA)-Based Composite Membranes Using Carboxyl-Type Boronic Acid Copolymers for Alkaline Diffusion Dialysis

Lizhen Peng,Xiaonan Huang,Dandan Liu,Jibin Miao,Bin Wu,Ming Cao,Qianqian Ge,Bin Yang,Lifen Su,Ru Xia,Zhengzhi Zheng,Peng Chen,Jiasheng Qian
DOI: https://doi.org/10.3390/polym12102360
IF: 5
2020-10-14
Polymers
Abstract:Carboxyl-type boronic acid copolymers (CBACs) were synthesized by a radical polymerization method and used for the preparation of polyvinyl alcohol (PVA)-based composite membranes via a solution mixture method. The as-prepared composite membranes exhibited a water uptake (WR) of 122.6–150.0%, an ion exchange capacity (IEC) of 0.0147–0.0518 mmol g−1, and excellent mechanical (elongation at break (Eb) of 103.8–148.4%, tensile strength (TS) of 38.7–58.6 MPa) and thermal stability. The alkali resistances of the as-prepared membranes were tested by immersing the samples into 2 mol L−1 NaOH solutions at 25 °C for 60 h, and the results were encouraging: the mass loss and swelling degree of the as-prepared membranes were in the ranges of 1.9–5.9% and 222.6–241.9%, respectively. The separation performances of the as-prepared membranes were evaluated by the diffusion dialysis (DD) process with an NaOH/Na2WO4 mixture at room temperature. The results demonstrated that the dialysis coefficients of hydroxide (UOH) were in the range of 0.0147–0.0347 m h−1, and the separation factors (S) were in the range of 29.5–62.6. The introduced carboxyl groups from CBACs and the –OH groups from PVA were both deemed to play significant roles in the promotion of ion transport: the –COO− groups formed negatively charged transport channels for Na+ by electrostatic attraction, and the –OH groups promoted the transport of OH− via hydrogen bonding.
polymer science
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve The paper aims to address the issue of membrane material selection and performance optimization in alkaline diffusion dialysis. Specifically, the researchers synthesized carboxylated boronic acid copolymers (CBACs) and used them to prepare polyvinyl alcohol (PVA)-based composite membranes to enhance the stability and separation performance of the membranes in alkaline environments. The main objectives include: 1. **Improving the water absorption rate (WR) of the membrane**: By introducing CBACs, the hydrophilicity of the membrane is enhanced, thereby increasing its water absorption capacity. 2. **Increasing the ion exchange capacity (IEC) of the membrane**: By introducing carboxyl and hydroxyl groups, the ion exchange capacity of the membrane is increased. 3. **Enhancing the mechanical properties and thermal stability of the membrane**: Ensuring that the membrane has good mechanical strength and heat resistance in practical applications. 4. **Improving the alkaline stability of the membrane**: Through crosslinking reactions, the stability of the membrane in strong alkaline environments is enhanced, reducing mass loss and swelling degree. 5. **Optimizing the separation performance of the membrane**: By adjusting the amount of CBACs added, the separation coefficient (UOH) and separation factor (S) of the membrane for hydroxide ions (OH⁻) and tungstate ions (WO₄²⁻) are optimized. In summary, the paper aims to develop high-performance membrane materials suitable for alkaline diffusion dialysis by synthesizing and characterizing novel carboxylated boronic acid copolymers and applying them to the preparation of PVA-based composite membranes.